牌号简介 About |
---|
TORZEN® U4664FL NC01是一种中等成核、润滑的PA66树脂,适用于注塑成型,需要快速结晶和快速循环时间。内部和外部都经过润滑,以获得良好的机器进料和模具释放。U4664FL还提供黑色。 TORZEN® U4664FL NC01 is a moderately nucleated, lubricated PA66 resin suitable for injection molding, where fast crystallization and fast cycle times are required. It is lubricated internally and externally for excellent machine feed and mold release. U4664FL is also available in black. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
2.0 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
1.8 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.8 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3200 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
2 mm 2 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.40 mm 0.40 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.71 mm 0.71 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.71 mm 0.71 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
教你打造更轻汽车和安全车内环境
2016-02-26 汽车轻量化对消费者所关注的安全性能、操控性能、环保性能等指标都有重要意义。3月10-11日,2016国际车用塑料暨汽车零部件产业链高峰论坛即将在上海举行。论坛聚焦“轻量化技术”和“安全车内环境”,力图推动国内汽车轻量化技术的资源整合及技术发展。 最为严苛的第四阶段燃油消耗标准已于2016年1月1日起实施。按照国家要求,到2020年,车企燃油限值要从2015年的6.9L/百公里降至5.0L/百公里,年均降幅达6.2%左右,这意味着目前1/4新车车型若不进行技术升级将面临淘汰。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |