牌号简介 About |
---|
Paryls PSU F3250GL30颗粒装在内衬铝箔袋的纸箱中,如果包装没有损坏,可以无限期储存。Paryls PSU F3250GL30颗粒吸收水分非常迅速。因此,在加工前,颗粒需要在真空或干燥空气干燥器中在160℃下干燥至少6h。特点Paryls PSU F3250GL30,树脂是一种30%玻璃纤维增强聚砜(PSU)。玻璃纤维大大提高了聚砜树脂的刚性、拉伸强度、抗蠕变、尺寸稳定性和耐化学性。高性能使这些树脂在许多工程应用中成为金属的有效替代品。 PARYLS® PSU F3250GL30 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PSU F3250GL30 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 160 °C in a vacuum or dry air drier prior to processing. Features PARYLS® PSU F3250GL30, resin is a 30% glass fiber reinforced polysulfone(PSU). Glass fiber substantially increasee the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties make these resins particularly effective alternatives to metals in many engineering applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
343℃,2.16kg 343℃,2.16kg |
5.0 到 10 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 , ISO 2577 | ||
TD TD |
0.45 | % | ISO 294-4,ISO 2577 |
MD MD |
0.30 | % | ISO 294-4,ISO 2577 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.20 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180/A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ISO 11357-2 , DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23℃ MD:23℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 3 |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity 3 |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 4 |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
4.50 mm 4.50 mm |
UL 94 |
备注 |
---|
2 10°C/min |
3 100V |
4 K20/K20, (60*60*1 mm³) |
【新闻资讯】查看全部
中美合资企业Auria Solutions降生
2017-10-11 中美合资企业Auria Solutions有限公司于9月15日正式成立,提供汽车地毯和音响零部件。公司的成立要归功于一段长达十年的合作,美国的Brian Pour和中国的姚明华。 普尔现年45岁,是Auria公司的首席执行官,在其22年的职业生涯中,有18年在亚洲,先后任职于Textron汽车、李尔及国际汽车零部件集团IAT。IAT软饰事业部年销售收入约10亿美元、拥有7000名员工,在北美、亚洲和欧洲拥有21家工厂和四个技术中心。 姚明华现年56岁,代表A |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |