LNP Thermocomp Noryl_hm3020化合物是一种30%玻璃/矿物填充,高模量等级。DTUL 248F(120摄氏度)。UL94 V-1/5VA,黑色和灰色。 LNP THERMOCOMP NORYL_HM3020 compound is a 30% Glass/Mineral filled, high modulus grade. DTUL 248F (120C). UL94 V-1/5VA rated in black and gray. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
内部方法 | ||
MD:3.2 mm MD:3.2 mm |
0.25 | % | |
TD:3.2 mm TD:3.2 mm |
0.30 | % | |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.060 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
91 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ||
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1.6 mm,在空气中 1.6 mm in air |
kV/mm | ASTM D149 | |
耐电弧性 Arc resistance 5 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.47 mm 1.47 mm |
|||
2.59 mm 2.59 mm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸强度 tensile strength 1 |
|||
断裂 fracture 1 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
100 mm跨距 100 mm span 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,100 mm跨度 Yield, 100 mm span 4 |
MPa | ASTM D790 | |
泊松比 Poisson's ratio |
ASTM D638 | ||
摩擦系数 friction coefficient |
ASTM D1894 | ||
与钢 - 静态 Steel - Static |
|||
与自身 - 静态 With oneself - static |
|||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 0.20 in/min |
3 0.10 in/min |
4 钨电极 |
【新闻资讯】查看全部
资料研发增强惠普塑料行业竞争力
2017-04-11 惠普一直致力于3D打印技术、材料的研发。上周,惠普采用材料开放平台的策略,鼓励材料领域的合作伙伴开发与惠普的系统兼容的粉末材料。这也是3D打印领域最新的里程碑。 惠普新的3D开放材料和应用实验室位于俄勒冈州的科瓦利斯,是一个3500平方英尺的空间,在这里工程师们一起开发、测试与反馈材料性能。为此,惠普提出了进入12万亿美元制造领域的3D打印战略。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-LNP™ THERMOCOMP™ Noryl_HM3020 compound证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)