产品细节:超高性能热塑性聚合物、30%PBI-PEK共混玻璃纤维、适合注塑和挤出成型的半结晶颗粒、易流动、颜色呈深绿色。应用领域:适用于超高负荷下的高温应用,优异的耐磨性,适用于半导体应用和等离子体处理设备。 Product Details: Ultra high performance thermoplastic polymer, 30% glass fiber reinforced in PBI PEK Blend, semi-crystalline granules suitable for injection molding as well as extrusion, easy flow, dark green in color. Application Areas: Suitable for high temperature applications under extremely high load, Excellent wear resistance, suitable for semiconductor applications and plasma handling equipments. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.55 | g/cm³ | |
收缩率 Shrinkage rate 2 |
|||
TD TD 2 |
0.58 | % | |
MD MD 2 |
0.20 | % | |
吸水率 Water absorption rate |
|||
平衡 balance |
0.24 | % | ASTM D570 |
螺旋流动长度 Spiral flow length 2 |
4.50 | cm | ASTM D3123 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
连续使用温度 Continuous use temperature |
℃ | UL 746B | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加热减量 Heating reduction |
Internal Method | ||
5% Weight Loss in Air 5% Weight Loss in Air |
℃ | Internal Method | |
5% Weight Loss in Nitrogen 5% Weight Loss in Nitrogen |
℃ | Internal Method | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
A 级 A-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 445°C nozzle, 220°C Mold |
【新闻资讯】查看全部
白金汉宫宣布新的渣滓处理方案
2018-09-14 近期,英国媒体报道,白金汉宫方面宣布新的垃圾处理计划,表示女王已经下令,禁止在王室产业内使用塑料吸管和塑料瓶,以减少塑料垃圾。一位欧盟委员会可持续发展问题的主管表示,如果不改变生产和使用塑料的方式,到2050年,海洋中的塑料垃圾数量将比鱼还要多。 塑料几乎是引起环境污染最严重的一类合成材料。E20研究院固废产业研究中心负责人潘功告诉《中国科学报》记者,这一点都不危言耸听。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |