由Ensinger制造的Delrin570型是20%的玻璃填充材料,用于一般工业用途。该材料具有很高的刚度、较低的翘曲和较低的蠕变,在应力作用下具有优异的零件性能。Delrin570用于汽车或建筑等多种行业,在这些行业中需要增加强度和刚度。非常好的尺寸稳定性玻璃纤维提供了刚度,但没有增强良好的可加工性。 DELRIN® 570 Shapes manufactured by Ensinger are 20% glass filled materials intended for general industrial use. The material offers very high stiffness, low warpage, and low creep for superior part performance under stress. DELRIN® 570 is used in a variety of industries such as automotive or construction where added strength and stiffness are desirable. Very good dimensional stability Glass fibers offer stiffness but not reinforcement Good machinability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.56 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
48 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
165 | ℃ | |
1.8 MPa,未退火 1.8 MPa, unannealed |
155 | ℃ | |
熔融温度 Melting temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
使用温度 Operating temperature |
|||
Intermittent Intermittent |
℃ | ||
长期 long-term |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 2 |
|||
23 ℃,60 Hz 23 ℃,60 Hz 2 |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ||
断裂,23℃ Fracture, 23 ℃ |
% | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
压缩强度 compressive strength |
|||
10% 应变,23℃ 10% strain, 23 ℃ |
MPa | ASTM D695 |
备注 |
---|
2. 50% RH |
【新闻资讯】查看全部
中低端制造业外移风险有多大?这些教训值得深思
2021-05-24 搜料网资讯: 新冠疫情之后传统意义上的全球化可能减速,产业链的转移和重置成为当前经济学界重点关注的问题。中国是国际生产网络的主要组成部分,不加控制的产业链转移会给中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |