牌号简介 About |
---|
SABIC PC PC5800树脂PC5800树脂是一种非常高流量(mfr=8.9,250c/1.2kg)的聚碳酸酯产品,设计用于光学介质市场。仅在www.sabicpc.com上提供。 PC5800 resin is a very high flow (MFR = 8.9 at 250C/1.2kg) polycarbonate product designed for use in the optical media market. It is available exclusively at www.sabicpc.com. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.20 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
250℃,1.2 kg 250℃,1.2 kg |
8.9 | g/10min | ASTM D1238 |
300℃,1.2 kg 300℃,1.2 kg |
58 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
250℃,1.2 kg 250℃,1.2 kg |
8.0 | cm³/10min | ISO 1133 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
MD MD |
0.50 到 0.70 | % | 内部方法 |
吸水率 Water Absorption Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
50 mm/m 50 mm/m |
MPa | ASTM D638 | |
1 mm/min 1 mm/min |
MPa | ISO 527-1-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
-- -- |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
B50 B50 |
℃ | ISO 306/B50, ASTM D1525 14 | |
球压测试 Ball Pressure Test Ball Pressure Test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD MD |
|||
-40 到 95℃ -40 to 95 ℃ |
cm/cm/℃ | ASTM E831 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
W/m/K | ASTM C177, ISO 8302 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | IEC 60093 | |
相对电容率 Relative Permittivity Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive Index Refractive Index |
ASTM D542,ISO 489 | ||
透光率 Light Transmission Light Transmission |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 2.0 in/min |
4 类型 1, 2.0 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 80*10*3 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部 ![]()
百吨级高强高模聚酰亚胺纤维项目通过鉴定
2022-03-23 3月21日,百吨级高强高模聚酰亚胺(PI)纤维制备技术及应用项目在北京通过了由中国石油和化学工业联合会组织的科技成果鉴定。由中国工程院院士曹湘洪、陈祥宝、蹇锡高,中国科学院 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |