| 牌号简介 About |
|---|
| Ultramid® A3X2G5是一种25%玻璃纤维增强注塑成型PA66级，具有改进的阻燃性和增强的长期性能。基于红磷的阻燃剂；优异的机械和电气性能。 Ultramid A3X2G5 is a 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term performance. Flame retardant based on red phosphorus; outstanding mechanical and electrical properties. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 耐油; 阻燃; 电气性好; Good Electrical Properties,Flame Characteristics,Grease resistance,V-0
填料：玻璃纤维 25
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.34 | g/cm³ | ASTM D792 |
|
密度 Density |
1.34 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
275℃，5 kg 275℃，5 kg |
40.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.50 | % | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
6.0 | % | ISO 62 |
|
饱和 saturated |
% | ASTM D570 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
平衡，50% RH Balance, 50% RH |
% | ASTM D570 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂，-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-40℃ -40℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ||
|
MD MD |
1/℃ | ASTM E831 | |
|
MD MD |
1/℃ | ||
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
UL 746 | ||
|
0.40 mm 0.40 mm |
℃ | UL 746 | |
|
0.8 mm 0.8 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
UL 746 | ||
|
0.8 mm 0.8 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
UL 746 | ||
|
0.40 mm 0.40 mm |
℃ | UL 746 | |
|
0.8 mm 0.8 mm |
℃ | UL 746 | |
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.80 mm 0.80 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
塑料制品会因着色剂不耐低温而发作分解褪色
2017-08-29 塑料制品行业发展越来越快，我们生活中到处可见。有时候会发现着色的塑料制品会发生颜色变化，这是为什么呢? 塑料成型加工时，着色剂因不耐高温而发生分解褪色变色 用于塑料着色的颜料或染料均存在耐温极限，达到这一极限温度，颜料或染料将发生化学变化，生成各种较低分子量化合物，其反应式均较复杂;不同的颜料存在不同的反应及产物，通过失重等分析方法可以检测不同颜料的耐温性 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |