牌号简介 About |
---|
挤出和注射成型用高粘度聚对苯二甲酸丁二醇酯 Unreinforced High Viscosity Polybutylene Terephthalate Developed for Extrusion and Injection Molding |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2600 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
57.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
屈服 yield |
4.0 | % | ISO 527-2 |
标称拉伸断裂应变 Nominal tensile fracture strain |
> 50 | % | ISO 527-2 |
弯曲强度 Flexural Strength |
85.0 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
可燃性等级 Flammability level |
IEC 60695-11-10, -20 | ||
1.5 mm 1.5 mm |
IEC 60695-11-10, -20 | ||
3.0 mm 3.0 mm |
IEC 60695-11-10, -20 | ||
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
FMVSS 阻燃等级 FMVSS flame retardant rating |
FMVSS 302 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
有机化合物的排放 Emissions of organic compounds |
µgC/g | VDA 277 | |
Odor Odor |
VDA 270 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,2.16kg 250℃,2.16kg |
g/10min | ISO 1133 | |
收缩率 Shrinkage |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
顶出温度 Ejection temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
3 FMVSS 302 |
【新闻资讯】查看全部 ![]()
国内石化企业产能使用率约在90.5%
2018-08-16 国内石化企业产能利用率约在90.5%,较上周略微下降。其中,华东地区产能利用率下降,华东地区湖南长盛临时停车,计划本周内重启;其它地区石化装置开工稳定,产能利用率变化不大。截至8月10日,国内聚丙烯装置检修损失量大幅增加 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |