牌号简介 About |
---|
SABIC® LDPE 2308N0是不含添加剂的低密度聚乙烯管级。SABIC® LDPE 2308N0采用SABIC清洁管式反应器(CTR)技术生产,确保产品纯度高。它具有高韧性、良好的柔韧性和合理的抗环境应力开裂性,因此通常用于柔韧性和坚硬物品。应用注射成型:SABIC® LDPE 2308N0通常适用于注射成型应用,常用于盖和封口。母料配制:SABIC® LDPE 2308N0通常用作母料和配制应用的载体树脂。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LDPE 2308N0 is a LDPE tubular grade without additives. SABIC® LDPE 2308N0 is produced using SABIC Clean Tubular Reactor (CTR) Technology which ensure grades with high purity. It exhibits high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore typically used for flexibles and tough articles. Application Injection Molding: SABIC® LDPE 2308N0 is typically suitable for injection moulding application, frequently used for Caps & closures. Masterbatch Compounding: SABIC® LDPE 2308N0 is typically suitable as carrier resin for masterbatch and compounding applications. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
7.5 | g/10min | |
190℃,5.0kg 190℃,5.0kg |
25 | g/10min | |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
10.0 | cm³/10min | |
190℃,5 kg 190℃,5 kg |
33.0 | cm³/10min | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ||
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | DIN 53765 | |
Enthalpy Change Enthalpy Change |
J/g | DIN 53765 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
MPa | ISO 527-2/1A/50 | |
拉伸强度 tensile strength |
ISO 527-2/1A/50 | ||
屈服,注塑成型 Yield, injection molding |
MPa | ||
断裂,注塑成型 Fracture, injection molding |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,注塑成型 Fracture, injection molding |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
莫斯科举行Interplastica展会
2018-12-20 2019年1月29至2月1日,在莫斯科举行的Interplastica展会中,威猛巴顿菲尔将在2.1/A23展位,展示其最新的注塑成型技术及自动化和辅助设备。 在2019 Interplastica展会中,威猛巴顿菲尔将展示其配备了最新威猛模内贴标(IML)单元的新的EcoPower Xpress 160/1100+注塑机。 EcoPower Xpress是一款全电动、高速和高性能的注塑机,专为包装行业所需的高产量薄壁应用而 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |