公司信息及水印
牌号简介 About |
---|
solef ® 6012 PVDF均聚物是一种高粘度PVDF树脂,通常采用挤塑或模压成型加工。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.75 to 1.80 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
230℃,10.0kg 230℃,10.0kg |
4.0 to 7.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage Shrinkage rate |
|||
MD MD |
2.0 to 3.0 | % | |
吸水率 Water Absorption Water Absorption |
|||
23℃,24hr 23℃,24hr |
< 0.040 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D,1 秒,2.00 mm Shore D, 1 second, 2.00 mm |
72 to 78 | ASTM D2240 | |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃,2 mm 23℃,2 mm |
MPa | ASTM D638 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂,23℃,2 mm Fracture, 23 ℃, 2 mm |
MPa | ASTM D638 | |
屈服,23℃,2 mm Yield, 23 ℃, 2 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂,23℃,2 mm Fracture, 23 ℃, 2 mm |
% | ASTM D638 | |
屈服,23℃,2 mm Yield, 23 ℃, 2 mm |
% | ASTM D638 | |
摩擦系数 Frictional coefficient Frictional coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
ASTM D1894 | ||
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
泰伯耐磨性 Taber Abrasion Taber Abrasion |
|||
1000 周期,1000 g,CS-10 转轮 1000 cycles, 1000 g, CS-10 wheels |
mg | ASTM D4060 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃,4mm 23℃,4mm |
J/m | ASTM D6110 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ASTM D4065 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 5 | |
熔融温度 Melting temperature Melting temperature |
℃ | ASTM D3418 | |
峰值结晶温度(DSC) Peak Crystallization Temperature (DSC) Peak Crystallization Temperature (DSC) |
|||
DSC DSC |
℃ | ASTM D3418 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:0~40℃ MD:0~40℃ |
1/℃ | ASTM D696 | |
比热 Specific Heat Specific Heat |
ASTM E968 | ||
23℃ 23℃ |
J/kg/℃ | ASTM E968 | |
100℃ 100℃ |
J/kg/℃ | ASTM E968 | |
导热系数 Thermal Conductivity Thermal conductivity |
|||
23℃ 23℃ |
W/m/K | ASTM C177 | |
结晶热 Crystallization Heat Crystallization Heat |
J/g | ASTM D3417 | |
熔化热 Heat of Fusion Heat of Fusion |
J/g | ASTM D3417 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
23 ℃,1 kHz 23 ℃,1 kHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
0.10 mm 0.10 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
|||
3.0 mm 3.0 mm |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 0.039 in/min |
3 类型 4, 2.0 in/min |
4 2 m/s |
5 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
如何稳投资稳外资?国家发改委这样回应
2021-09-09 搜料网资讯: 做好稳投资、稳外资备受社会各界关注。国家发展改革委8日举行专题新闻发布会,对当前我国投资和外资形势作出回应。 投资仍然具备保持稳定增长的条件 今年前7个月, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |