牌号简介 About |
---|
SUMIKASUPER® LCP E6006L是一种热致液晶聚酯,在工程塑料中表现出最高的耐热性 SUMIKASUPER® LCP E6006L is a Liquid Crystal Polymer (LCP) material filled with glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of SUMIKASUPER® LCP E6006L: Flame Rated. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.61 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD |
0.19 | % | 内部方法 |
TD TD |
0.74 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和 saturated |
0.020 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
140 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
6.4 mm 6.4 mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
内部方法 | ||
MD:150℃ MD:150℃ |
1/℃ | 内部方法 | |
TD:150℃ TD:150℃ |
1/℃ | 内部方法 | |
导热系数 Thermal conductivity coefficient |
W/m/K | JIS R2618 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.30 mm,本色,黑色 0.30 mm, natural color, black |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | JIS K7201 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Soldering Resistance Soldering Resistance |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ASTM D790 | |
200℃ 200℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
屈服,200℃ Yield, 200 ℃ |
MPa | ASTM D790 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
过量塑化剂影响生殖 精子库专家:少用塑料容器
2017-02-22 不想做饭就叫个外卖,有没有想过装着外卖食物的塑料碗会对身体不利?在家用微波炉加热食物,有没有将塑胶包装替换成玻璃器皿?这些不经意,都可能让塑化剂不知不觉进入体内。上海市人类精子库生殖男科专家陈向锋副主任医师表示,过量的塑化剂会干扰人类内分泌系统,影响生殖功能,无论男女。 近年来,科学家怀疑被广泛用于产品增塑剂的邻苯二甲酸酯会干扰人类内分泌特别是生殖功能,过去几十年男性精子数量的减少可能与摄入这类人工合成化学品有关。陈向锋支持这个观点,但人体一般情况下会从环境中吸收多少邻苯二 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |