| 牌号简介 About |
|---|
| Titanvene™ LL0209SC是一种线性低密度聚乙烯，用于高清晰度薄膜应用。Titanvene™ LL0209SC具有透明性好、凝胶含量低、加工性能好、机械性能好、阻隔力低、滑移率高等特点。应用工业包装购物袋食品包装米袋透明膜服装袋建议的加工条件Titanvene™ LL0209SC可以很容易地在正常的聚乙烯吹膜机在170°C到200°C的温度范围内加工。食品接触合规性Titanvene™ LL0209SC可用于食品接触应用。请联系最近的患者。Lotte Chemical Titan Nusantara代表详细了解特定等级的食品接触合规声明。 Titanvene™ LL0209SC Titanvene™ LL0209SC is a linear low density polyethylene for high clarity film application. Titanvene™ LL0209SC is characterized by excellent transparency, low gel content, good process ability, and good mechanical properties with low blocking force and high slip. Applications Industrial packaging Shopping bags Food packaging Rice Bag Transparent Film Garment Sack Recommended Processing Conditions Titanvene™ LL0209SC can be easily processed on normal polyethylene blow film machines at temperatures in the range of 170°C to 200°C. Food Contact Compliance Titanvene™ LL0209SC can be used in food contact applications. Please contact your nearest PT. Lotte Chemical TITAN Nusantara representative for more detail of food contact compliance statements for the specific grade. Titanvene™ LL0209SC Titanvene™ LL0209SC is a linear low density polyethylene for high clarity film application. Titanvene™ LL0209SC is characterized by excellent transparency, low gel content, good process ability, and good mechanical properties with low blocking force and high slip. Applications Titanvene™ LL0209SC is typically used for : Industrial Packaging - Shopping Bags Food Packaging - Rice Bag Transparent Film - Garment Sack |
产品描述 Product Description
用途：薄膜;包装;袋子;食品包装;
颜色：清晰/透明
加工条件：吹塑薄膜
性能特点： 低速凝固晶点; 高光滑性; 透光性好; 食品接触; 易加工; Excellent Processability,Good Clarity,Smoothness,Low speed solidification point,Food contact compliance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.920 | g/cm³ | ISO 1183/D |
|
熔体质量流动速率 Melt Flow Rate 2 |
|||
|
190℃，2.16kg 190℃，2.16kg 2 |
1.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient 3 |
0.14 | BS 2782 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness 4 |
|||
|
测试 test 4 |
38 | µm | |
|
拉伸强度 tensile strength 5 |
ISO 1184 | ||
|
MD，屈服，38 µm，吹塑薄膜 MD, yield, 38 µ m, blow molded film |
11.0 | MPa | ISO 1184 |
|
TD，屈服，38 µm，吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ISO 1184 | |
|
拉伸应变 Tensile strain 5 |
ISO 1184 | ||
|
MD，断裂，38 µm，吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ISO 1184 | |
|
TD，断裂，38 µm，吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ISO 1184 | |
|
落锤冲击 Drop hammer impact |
|||
|
38 µm，吹塑薄膜 38 µ m, blow molded film |
g | ISO 7765-1/A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
|
熔融温度 Melting temperature 6 |
|||
|
DSC DSC 6 |
℃ | ISO 3146 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
透明度 transparency |
ASTM D1746 | ||
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Condition 4 |
| 3 Method 824A |
| 4 BUR 2:1 |
| 5 Speed 1 |
| 6 Method C |
|
【新闻资讯】查看全部 
一种可替代钛白粉的复合钛白颜料面世
2021-10-24 搜料网资讯： 日前，一种的替代产品TCA复合钛白颜料在北京天之岩健康科技有限公司研制成功。目前，该产品目前已经完成中试和应用实验。通过了由北京市科委组织的省部级鉴定，产 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付