牌号简介 About |
---|
说明:LL318是一种线性低密度聚乙烯,丁烯-1共聚物,采用滚圆法生产。开发用于铸膜挤出。用该产品制备的薄膜具有良好的力学性能和密封性。它含有抗氧化添加剂。用途:拉伸薄膜;衬里;低密度聚乙烯和高密度聚乙烯混合物和普通用途的包装。 LL318 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by Spherilene process. Developed for cast film extrusion. Films obtained with this product show good mechanical properties and enhanced sealability. It contains antioxidant additives. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.7 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
1400 | % | ASTM D882 |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,38 µm,吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
g | ASTM D1922 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,38.0 µm,吹塑薄膜 60 °, 38.0 µ m, blow molded film |
ASTM D2457 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美国将征收出口车和汽车零部件关税
2018-09-12 根据《日经新闻》近日的报道,基于美中贸易战当前未有缓和趋势,美国也正考虑征收进口车和汽车零部件关税,日本各企业开始撤出在中国的供应链。 日本化工企业旭化成(Asahi Kasei)计划将制造汽车零部件的中国厂迁回日本,因其制造的产品名列在美国的关税清单中。 与此同时,世界排名第2的重化工业产品制造公司小松制作所(Komatsu)将改用在美国、日本和墨西哥的设施生产液压挖土机零部件,而这些部件目前都在中国制造。但改变生产计划,将使小松制作所每年承受庞大的额外开 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |