| 牌号简介 About |
|---|
| Durethan® BC 700 HTS DUSXBL 900116 是一种热老化稳定的抗冲改性聚酰胺PA 6共聚物。具有高机械强度，良好的电绝缘性能，改进的冲击强度和高刚度。同时具有良好的韧性，低摩擦，动态承载性能和良好的加工性。用吹塑加工成型方式，适用于汽车，电气/电子行业，建筑和建筑行业。符合REACH和RoHS。 Durethan® BC700HTS 900116 DUSXBL (Dry) PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.durethan-tank-systems.lanxess.com . Durethan® BC700HTS 900116 DUSXBL PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.durethan-tank-systems.lanxess.com . Durethan® BC700HTS 900116 DUSXBL PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.us.durethan-tank-systems.lanxess.com . |
产品描述 Product Description
用途：水箱;
加工条件：吹塑成型
性能特点： 热稳定性好; 共聚物; 冲击性能好; 耐老化; Heat Stabilized,Good heat aging resistance,Copolymer,High impact resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.03 | g/cm³ | ISO 1183 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
8.1 | % | ISO 62 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
1.9 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
65 | ISO 868 | |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
980 | MPa | ISO 527-1-2 |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178-A | |
|
弯曲强度 bending strength |
|||
|
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲应变 Bending strain |
% | ||
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
膜刺穿强度 Membrane puncture strength |
ISO 6603-2 | ||
|
-- -- |
J | ISO 6603-2 | |
|
-- -- |
J | ISO 6603-2 | |
|
膜刺穿力 Membrane puncture force |
ISO 6603-2 | ||
|
-- -- |
N | ISO 6603-2 | |
|
-- -- |
N | ISO 6603-2 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
|
-30℃ -30℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~55℃ TD：23~55℃ |
1/℃ | ISO 11359-2 | |
|
MD：23~55℃ MD：23~55℃ |
1/℃ | ISO 11359-2 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
ISO Shortname ISO Shortname |
ISO 1874 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.079 in/min |
| 3 2 mm/min |
| 4 Pull Rate: 2 mm/min; 50% RH |
| 5 -30°C |
| 6 23°C |
| 7 10°C/min |
|
【新闻资讯】查看全部 
扬子石化茂金属聚乙烯家族再添新成员
2021-04-07 搜料网资讯： 4月1日，扬子石化在2号聚乙烯装置上成功实现了茂金属中密度重包装膜料mPE F331F首次工业化生产。经检测，产品性能达到设计要求。 这是该公司继茂金属重包装膜mPE-L F1 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付