| 牌号简介 About |
|---|
| Promyde® B30 U是一种聚酰胺6阻燃剂，UL认证，热稳定，有核和润滑。特点Promyde® B30 U是一种改进的阻燃聚酰胺6，UL认证，热稳定，润滑和成核快速循环注塑成型。它的主要特点是易于流动，易于模具填充和非常快的冷却时间，同时保持良好的聚酰胺6机械性能。由于其改进的热线可燃性指数为960°C，易于流动的特点和非常快的冷却时间，应用；Promyde® B30 U适用于汽车、电气、电子或技术零件等阻燃零件的多腔和单腔注射成型。 Promyde B30 U is a Polyamide 6 flame retardant, UL certified, heat stabilised, nucleated and lubricated. CHARACTERISTICS Promyde B30 U is an improved flame retardant polyamide 6, UL certified, heat stabilized, lubricated and nucleated for fast cycle injection moulding. Its main characteristics are easy flowing, easy mould filling and very fast cooling time whilst maintaining excellent polyamide 6 mechanical properties. APPLICATIONS Due to its improved Glow Wire Flammability Index of 960°C, easy flow characteristics and very fast cooling time; Promyde B30 U is suitable for multi cavity and single cavity injection moulding of flame resistant parts such as components used in automotive, electrical, electronics, or technical parts. |
产品描述 Product Description
用途：电气元件;工程配件;汽车领域的应用;电气/电子应用领域;
加工条件：注射成型 Injection Molding
性能特点： 成核的; 热稳定性好; 含脱模剂; 成型周期快; 防火阻燃等级V-2; 润滑性; 阻燃; 易流动; 易加工; Lubricating,Good stripping performance,Flame Characteristics,Good liquidity,Heat Stabilized,V-2,Excellent Processability,Quick molding cycle,Nucleation
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.13 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
275℃，5 kg 275℃，5 kg |
145 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
TD TD |
0.80 to 1.1 | % | |
|
MD MD |
0.90 to 1.1 | % | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
9.5 | % | ISO 62 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
粘数 Viscosity number |
cm³/g | ISO 307 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
|
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
|
23℃ 23℃ |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~80℃ TD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.079 in/min |
| 3 10°C/min |
|
【新闻资讯】查看全部 
霍尼韦尔工厂投产车用低温室效应制冷剂 2017-05-24 据外媒报道，因全球对低温室效应汽车空调的需求量不断加大，霍尼韦尔近日表示将在投资3亿美元组建的路易斯安娜州Geismar工厂生产Solstice yf制冷剂。 霍尼韦尔 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付