EVA树脂Alcudia PA-442适用于低粘度热熔胶粘剂,可与各种粘树脂和蜡相容。它含有抗氧化剂和自由流动剂。典型应用热熔胶包装装订建议熔化温度低于200°C,以避免聚合物分解。各生产线的加工条件应得到优化。 Special Epoxy Molding Compounds Optimizing Warpage and Applicable to Fine Pitch Wire for BGA Package Strong Points Less Warpage in All Types of Area Array Packages due to High Tg Characteristic. Applicable to Fine Pitch Wire Bonding with Good Wire Sweep Performance. Achieve High Yield after Molding due to Excellent Moldability that allows its application to MAP. Application Standard P-BGA, HS-BGA and LGA Package. Multi Chip Module (Stacked or Side by Side Layout) IC Card, Memory Card etc. Low Alpha Ray Type: KE-2150 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.00 | g/cm³ | |
螺旋流动长度 Spiral flow length |
190 | cm | |
溶液粘度 Solution viscosity |
5000 | mPa·s | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
18000 | MPa | |
弯曲强度 bending strength |
150 | MPa | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-- -- 3 |
cm/cm/℃ | ||
-- -- 4 |
cm/cm/℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blend 40:60 PA-441/wax |
【新闻资讯】查看全部
洛阳石化百万吨乙烯项目可研报告进入评估阶段
2021-10-24 搜料网资讯: 近日,中国石化集团公司在北京召开会议,邀请中国化工学会、中国合成橡胶工业协会等10余个单位专家,以及相关代表组成评估专家组,分别对洛阳石化百万吨 乙烯 项目 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |