| 牌号简介 About |
|---|
| 产品描述：SABLC LDPE HPO823J是一种低密度聚乙烯级，采用防滑和防堵添加剂配制而成。它通常表现出良好的熔融强度和良好的下拉能力。薄膜具有良好的韧性和双轴收缩性能，摩擦小，堵塞小。典型应用：收缩膜，工业薄膜，包装薄膜，袋子。该等级可实现高速转换，无需粘贴。本产品不适用于医疗和制药应用。 PRODUCT DESCRIPTION: SABlC® LDPE HPO823J is a Low Density Polyethylene grade formulated with slip and anti-block additives. It typically exhibits good melt strength with good draw down ability. Films typically exhibit good toughness and good biaxial shrink properties with low friction and low blocking. TYPICAL APPLICATIONS: Shrink film, thin industrial film, thin packaging film, bags & pouches. This grade enables high speed converting without sticking. This product is not intended for use in medical and pharmaceutical applications. |
产品描述 Product Description
用途：薄膜;包装;工业应用;袋子;收缩性薄膜;
加工条件：吹塑薄膜
性能特点： 抗结块性; 熔体强度好; 高光滑性; 易剥离; 食品接触; 低摩擦系数; 低密度; 韧性好; Good flexibility,Smoothness,Good dissection,Low coefficient of friction,High anti-blocking,Food contact compliance,Good melt strength,Low density
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.923 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.80 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
0.05 mm 0.05 mm |
260 | MPa | ISO 527-2 |
|
摩擦系数 friction coefficient |
< 20 | % | ISO 8295 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
薄膜厚度 film thickness |
|||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
屈服，0.05 mm Yield, 0.05 mm |
MPa | ISO 527-2 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
20°，50 µm，吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
|
60°，50.0 µm，吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blow（up Ratio） Blow（up Ratio） |
|||
| 备注 |
|---|
| 1 Erucamide |
| 2 Natural Silica |
| 3 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
超薄！科思创在K 2022上展示其新产品Makrofol®TF超薄聚碳酸酯挤压薄膜
2022-10-21 扫描上图二维码，可以免费下载 搜料 APP 科思创将于 10 月 19 日至 26 日在德国杜塞尔多夫举行的 K 2022 塑料贸易展览会上向业界展示厚度仅为 15% 的新型聚碳酸酯（PC）薄膜，厚度仅为 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付