| 牌号简介 About |
|---|
| Ultramid A 20 V25是一种基于聚酰胺66树脂的25%玻璃纤维增强红磷阻燃等级。本产品经过热稳定处理，以优化注塑成型。本产品为天然和黑色。 TECHNYL® A 20 V25 Natural is a Red Phosphorous flame retardant polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection moulding. This grade provides robust UL 94 V-0 and a full UL yellow card while offering good mechanical properties. This grade is suitable for moulding insulating parts for electrical devices, and more generally for thin parts under stress. |
产品描述 Product Description
用途：电气/电子应用领域;工业应用;薄壁部件;绝缘材料;
颜色：黑色,自然色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 热稳定性好; 阻燃; Flame Characteristics,Heat Stabilized,V-0
填料：玻璃纤维 25
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density Density |
1.38 | g/cm³ | ISO 1183/A |
|
吸水率 Water absorption Water absorption |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
2.1 | % | ISO 62 |
|
23℃，24hr 23℃，24hr |
0.75 | % | ISO 62 |
|
成型收缩率 Molding shrinkage Molding shrinkage |
|||
|
平行 parallel Parallel |
0.35 | % | |
|
垂直 normal Vertical normal |
1.2 | % | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus Tensile modulus |
|||
|
23℃，干燥 dry 23 ℃, dry |
MPa | ISO 527-2/1A | |
|
23℃，湿润 cond. |
MPa | ISO 527-2/1A | |
|
拉伸强度 Tensile Stress Tensile Strength |
|||
|
断裂 break，23℃，干燥 dry Break, 23 ℃, dry dry |
MPa | ISO 527-2/1A | |
|
断裂 break，23℃，湿润 cond. Break, 23 ℃, wet cond |
MPa | ISO 527-2/1A | |
|
拉伸应变 Tensile Strain Tensile Strain |
|||
|
断裂，23℃，干燥 dry Fracture, 23 ℃, dry dry |
% | ISO 527-2 | |
|
断裂，23℃，湿润 cond. Fracture, 23 ℃, wet cond |
% | ISO 527-2 | |
|
弯曲模量 Flexural modulus Flexural modulus |
|||
|
23℃，干燥 dry 23 ℃, dry |
MPa | ISO 178 | |
|
23℃，湿润 cond. 23 ℃, moist cond |
MPa | ISO 178 | |
|
弯曲强度 Flexural strength Flexural strength |
|||
|
23℃，干燥 dry 23 ℃, dry |
MPa | ISO 178 | |
|
23℃，湿润 cond. 23 ℃, moist cond |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy notched impact strength Charpy notched impact strength |
|||
|
-30℃，干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eA | |
|
23℃，干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eA | |
|
23℃，湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eA | |
|
简支梁冲击强度 Charpy impact strength Charpy impact strength of simply supported beams |
ISO 179/1eU | ||
|
-30℃，干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eU | |
|
23℃，干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eU | |
|
23℃，湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Izod notched impact strength Izod notched impact strength |
|||
|
23℃，干燥 dry 23 ℃, dry |
kJ/m² | ISO 180/1A | |
|
23℃，湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT Hot deformation temperature HDT |
|||
|
1.8 MPa，未退火 unannealed 1.8 MPa, unannealed |
℃ | ISO 75-2/-1 | |
|
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-1/-3 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity Surface resistivity |
|||
|
干燥 dry Dry |
ohms | IEC 62631-3-2 | |
|
湿润 cond. Wet Cond |
ohms | IEC 62631-3-2 | |
|
体积电阻率 Volume resistivity Volume resistivity |
|||
|
干燥 dry Dry |
ohm·m | IEC 62631-3-1 | |
|
湿润 cond. Wet Cond |
ohm·m | IEC 62631-3-1 | |
|
介电强度 Electric strength Electric strength |
|||
|
0.8 mm 0.8 mm |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity Relative permittivity |
|||
|
干燥 dry，100Hz Dry, 100Hz |
IEC 62631-2-1 | ||
|
湿润 cond.，100Hz Wet Cond, 100Hz |
IEC 62631-2-1 | ||
|
耗散因数 Dissipation factor |
|||
|
干燥 dry Dry |
E-4 | IEC 62631-2-1 | |
|
湿润 cond. Wet Cond |
E-4 | IEC 62631-2-1 | |
|
相比漏电起痕指数 Comparative tracking index Compared tracking index |
|||
|
解决方案 A Solution A |
IEC 60112 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.80 mm 0.80 mm |
calss | UL 94 | |
|
1.60 mm 1.60 mm |
calss | UL 94 | |
|
3.20 mm 3.20 mm |
calss | UL 94 | |
|
灼热丝可燃性指数 Glow Wire Flammability Index Glow Wire Flammability Index |
IEC 60695-2-12 | ||
|
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
|
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
|
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Glow Wire Ignition Temperature |
|||
|
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Oxygen index |
% | ISO 4589-2 | |
|
French Fire Index French Fire Index |
NF F16-101 | ||
|
French Smoke Index French Smoke Index |
NF F16-101 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
亨斯迈子公司Venator宣布完成IPO
2017-08-11 美国亨斯迈公司(Huntsman)近日宣布，其旗下子公司Venator Materials PLC完成IPO，首次发行2610.5万股普通股。上周，Venator的普通股以股票代码VNTR在纽约证券交易所上市。 亨斯迈欲利用Venator债券发行产生的约7.25亿美元净收益以及约4.75亿美元IPO纯收益(不包括预付税)来抵消目前的公司债务。这样一来，12亿美元的巨额债务缩减将使亨斯迈净债务对EBITDA比率降到约2.5。而且，亨斯迈的年现金利息支出有望减少4500万美元。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付