PA66，Ultramid® A 20 V25 NATURAL对比PA66，Ultramid® A3X2G5物性表,价格行情_搜料

牌号信息	Ultramid® A 20 V25 NATURAL 物性表 PA66 & 德国巴斯夫指导价格：暂无塑料库存： 12000kg	Ultramid® A3X2G5 物性表 PA66 & 德国巴斯夫指导价格：44625.0元/吨塑料库存： 26050kg
牌号简介	Ultramid A 20 V25是一种基于聚酰胺66树脂的25%玻璃纤维增强红磷阻燃等级。本产品经过热稳定处理，以优化注塑成型。本产品为天然和黑色。 TECHNYL® A 20 V25 Natural is a Red Phosphorous flame retardant polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection moulding. This grade provides robust UL 94 V-0 and a full UL yellow card while offering good mechanical properties. This grade is suitable for moulding insulating parts for electrical devices, and more generally for thin parts under stress.	Ultramid® A3X2G5是一种25%玻璃纤维增强注塑成型PA66级，具有改进的阻燃性和增强的长期性能。基于红磷的阻燃剂；优异的机械和电气性能。 Ultramid A3X2G5 is a 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term performance. Flame retardant based on red phosphorus; outstanding mechanical and electrical properties.

产品描述
厂家：	德国巴斯夫 BASF	德国巴斯夫 BASF
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 25	玻璃纤维 25
用途：	工业应用,电气/电子应用领域,薄壁部件,绝缘材料
性能特点：	阻燃,热稳定性好,防火阻燃等级V-0 Flame Characteristics,Heat Stabilized,V-0	电气性好,阻燃,耐油,防火阻燃等级V-0 Good Electrical Properties,Flame Characteristics,Grease resistance,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位
UNIT 测试方法
TEST METHOD

吸水率 Water absorption(23℃，24hr)
Water absorption % ISO 62

吸水率 Water absorption(平衡，23℃，50% RH)
Water absorption % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，50% RH)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度 Density
Density g/cm³ ISO 1183/A

成型收缩率 Molding shrinkage(垂直 normal)
Molding shrinkage %

成型收缩率 Molding shrinkage(平行 parallel)
Molding shrinkage %

收缩率(MD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(275℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

机械性能
MECHANICAL Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位
UNIT 测试方法
TEST METHOD

弯曲强度 Flexural strength(23℃，干燥 dry)
Flexural strength MPa ISO 178

弯曲强度 Flexural strength(23℃，湿润 cond.)
Flexural strength MPa ISO 178

弯曲模量 Flexural modulus(23℃，干燥 dry)
Flexural modulus MPa ISO 178

弯曲模量 Flexural modulus(23℃，湿润 cond.)
Flexural modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变 Tensile Strain(断裂，23℃，干燥 dry)
Tensile Strain % ISO 527-2

拉伸应变 Tensile Strain(断裂，23℃，湿润 cond.)
Tensile Strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度 Tensile Stress(断裂 break，23℃，干燥 dry)
Tensile Strength MPa ISO 527-2/1A

拉伸强度 Tensile Stress(断裂 break，23℃，湿润 cond.)
Tensile Strength MPa ISO 527-2/1A

拉伸强度(断裂，-40℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量 Tensile modulus(23℃，干燥 dry)
Tensile modulus MPa ISO 527-2/1A

拉伸模量 Tensile modulus(23℃，湿润 cond. )
Tensile modulus MPa ISO 527-2/1A

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度 Izod notched impact strength(23℃，干燥 dry)
Izod notched impact strength kJ/m² ISO 180/1A

悬臂梁缺口冲击强度 Izod notched impact strength(23℃，湿润 cond.)
Izod notched impact strength KJ/m² ISO 180/1A

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁冲击强度 Charpy impact strength(-30℃，干燥 dry)
Charpy impact strength of simply supported beams kJ/m² ISO 179/1eU

简支梁冲击强度 Charpy impact strength(23℃，干燥 dry)
Charpy impact strength of simply supported beams kJ/m² ISO 179/1eU

简支梁冲击强度 Charpy impact strength(23℃，湿润 cond.)
Charpy impact strength of simply supported beams kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度 Charpy notched impact strength(-30℃，干燥 dry)
Charpy notched impact strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度 Charpy notched impact strength(23℃，干燥 dry)
Charpy notched impact strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度 Charpy notched impact strength(23℃，湿润 cond.)
Charpy notched impact strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位
UNIT 测试方法
TEST METHOD

热变形温度 HDT(1.8 MPa，未退火 unannealed)
Hot deformation temperature HDT ℃ ISO 75-2/-1

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度 Melting temperature
Melting temperature ℃ ISO 11357-1/-3

熔融温度(DSC)
Melting temperature ℃ ISO 3146

相对温度指数(0.40 mm)
Relative temperature index ℃ UL 746

相对温度指数(0.8 mm)
Relative temperature index ℃ UL 746

相对温度指数(1.5 mm)
Relative temperature index ℃ UL 746

相对温度指数(3.0 mm)
Relative temperature index ℃ UL 746

相对温度指数(冲击机械性能)
Relative temperature index UL 746

相对温度指数(强度机械性能)
Relative temperature index UL 746

相对温度指数(电气性能)
Relative temperature index UL 746

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃

电气性能
ELECTRICAL Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

介电强度 Electric strength(0.8 mm)
Electric strength kV/mm IEC 60243-1

体积电阻率 Volume resistivity(干燥 dry)
Volume resistivity ohm·m IEC 62631-3-1

体积电阻率 Volume resistivity(湿润 cond.)
Volume resistivity ohm·m IEC 62631-3-1

体积电阻率(1.50 mm)
Volume resistivity ohms·cm ASTM D257

相对电容率 Relative permittivity(干燥 dry，100Hz)
Relative permittivity IEC 62631-2-1

相对电容率 Relative permittivity(湿润 cond.，100Hz)
Relative permittivity IEC 62631-2-1

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数 Comparative tracking index(解决方案 A)
Compared tracking index IEC 60112

耗散因数 Dissipation factor (干燥 dry)
E-4 IEC 62631-2-1

耗散因数 Dissipation factor (湿润 cond.)
E-4 IEC 62631-2-1

耗散因数(1 MHz)
Dissipation factor IEC 60250

表面电阻率 Surface resistivity(干燥 dry)
Surface resistivity ohms IEC 62631-3-2

表面电阻率 Surface resistivity(湿润 cond.)
Surface resistivity ohms IEC 62631-3-2

阻燃性能
FLAMMABILITY Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位
UNIT 测试方法
TEST METHOD

French Fire Index
French Fire Index NF F16-101

French Smoke Index
French Smoke Index NF F16-101

极限氧指数 Oxygen index
% ISO 4589-2

灼热丝可燃性指数 Glow Wire Flammability Index(0.80 mm)
Glow Wire Flammability Index ℃ IEC 60695-2-12

灼热丝可燃性指数 Glow Wire Flammability Index(1.6 mm)
Glow Wire Flammability Index ℃ IEC 60695-2-12

灼热丝可燃性指数 Glow Wire Flammability Index(3.2 mm)
Glow Wire Flammability Index ℃ IEC 60695-2-12

灼热丝起燃温度 Glow Wire Ignition Temperature (1.6 mm)
℃ IEC 60695-2-13

阻燃等级(0.80 mm)
Flame retardant level calss UL 94

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level calss UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level calss UL 94

加工方式

注塑 Injection Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位测试方法

干燥温度 Drying Temperature °C

建议的最大水分含量 max allowed water content %

料筒中部温度 Injection molding cylinder temperature 2 °C

料筒前部温度 Injection molding cylinder temperature 3 °C

料筒后部温度 Injection molding cylinder temperature 1 °C

模具温度 Mold temperature °C ISO 294

注射 Ultramid® A 20 V25 NATURAL Ultramid® A3X2G5 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注塑 Injection
注射
备注
返回顶部

PA66，Ultramid® A 20 V25 NATURAL对比PA66，Ultramid® A3X2G5对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别