| 牌号简介 About |
|---|
| NORYL™ NHP6012树脂提供一流的非氯化/非溴化阻燃性，含有10%玻璃纤维；用途：电池模块电芯框架● 电池组顶盖● 电动汽车电池(EV)应用● 电池外壳● 电动车部件● 薄壁应用●薄壁产品。 |
产品描述 Product Description
用途：薄壁应用;电池;
性能特点： 尺寸稳定性好; 电气性能; 吸水率低; 流动性高; 低密度; Low density,Low or no water absorption,Good Dimensional Stability,High liquidity
填料：玻璃纤维 10
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
比重 proportion |
|||
|
|
1.19 | g/cm³ | ISO 1183 |
|
|
1.19 | g/cm³ | ASTM D 792 |
|
收缩率 Shrinkage rate |
|||
|
流动 flow |
0.5~0.7 | % | |
|
垂直 vertical |
0.5~0.7 | % | |
|
吸水率 Water absorption rate |
|||
|
23°C饱和 23 ° C saturation |
0.2 | % | ISO 62 |
|
23°C 24hr 23°C 24hr |
% | ISO 62 | |
|
23°C 50RH平衡 23 ° C 50RH balance |
% | ISO 62 | |
|
23°C 50RH 24hr 23°C 50RH 24hr |
% | ISO 62 | |
|
23°C饱和 23 ° C saturation |
% | ASTM D570 | |
|
23°C 24hr 23°C 24hr |
% | ASTM D570 | |
|
熔融指数 Melt index |
|||
|
280℃10kg 280℃10kg |
cm³/10min | ISO 1133 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M标尺 M scale |
ISO 2039 | ||
|
M标尺 M scale |
ASTM D785 | ||
|
球压硬度 Ball hardness |
|||
|
H358/30 H358/30 |
MPa | ISO 2039 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
1.0mm/min 1.0mm/min |
MPa | ISO 527 | |
|
5mm/min 5mm/min |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
断裂5mm/min Fracture 5mm/min |
MPa | ISO 527 | |
|
断裂5mm/min Fracture 5mm/min |
MPa | ASTM D638 | |
|
伸长率 elongation |
|||
|
断裂5mm/min Fracture 5mm/min |
% | ISO 527 | |
|
断裂5mm/min Fracture 5mm/min |
% | ASTM D638 | |
|
弯曲强度 bending strength |
|||
|
2.0mm/min 2.0mm/min |
MPa | ISO 178 | |
|
1.3mm/min 1.3mm/min |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
|||
|
2.0mm/min 2.0mm/min |
MPa | ISO 178 | |
|
1.3mm/min 1.3mm/min |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23°C 4.0mm 23°C 4.0mm |
KJ/m² | ISO 180 | |
|
-30°C 40mm -30°C 40mm |
KJ/m² | ISO 180 | |
|
23°C 23°C |
J/m | ASTM D256 | |
|
-30C -30C |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23°C 4.0mm 23°C 4.0mm |
KJ/m² | ISO 180 | |
|
-30°C 40mm -30°C 40mm |
KJ/m² | ISO 180 | |
|
23°C 23°C |
J/m | ASTM D4812 | |
|
-30C -30C |
J/m | ASTM D4812 | |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23°C 4.0mm 23°C 4.0mm |
kJ/m² | ISO 179 | |
|
23°C 4.0mm 23°C 4.0mm |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23°C 4.0mm 23°C 4.0mm |
kJ/m² | ISO 179 | |
|
-30°C 40mm -30°C 40mm |
kJ/m² | ISO 179 | |
|
仪表冲击 Instrument shock |
|||
|
23°C峰值能量 23 ° C peak energy |
J | ASTM D3763 | |
|
23°C总能量 23 ° C total energy |
J | ASTM D3763 | |
|
23°C峰值力 23 ° C peak force |
N | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1. 8MPa 4. 0mm 1. 8MPa 4. 0mm |
℃ | ISO 75 | |
|
0.45MPa 4 0mm 0.45MPa 4 0mm |
℃ | ISO 75 | |
|
未退火1. 8MPa 3.2mm Unannealed 1.8MPa 3.2mm |
℃ | ASTM D648 | |
|
未退火0.45MPa 3.2mm Unannealed 0.45MPa 3.2mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
50°C/hr 10N 50°C/hr 10N |
℃ | ISO 306 | |
|
50°C/hr 50N 50°C/hr 50N |
℃ | ISO 306 | |
|
120°C/hr 50N 120°C/hr 50N |
℃ | ISO 306 | |
|
50°C/hr 10N 50°C/hr 10N |
℃ | ASTM D1525 | |
|
50°C/hr 50N 50°C/hr 50N |
℃ | ASTM D1525 | |
|
120°C/hr 50N 120°C/hr 50N |
℃ | ASTM D1525 | |
|
线膨胀系数 Linear expansion coefficient |
|||
|
流动 -40 0~40°C Flowing -40 ° C to 40 ° C |
cm/cm/°C | ISO 11359 | |
|
垂直 -40.0~40°C Vertical -40.0~40 ° C |
cm/cm/°C | ISO 11359 | |
|
流动 -40 0~40°C Flowing -40 ° C to 40 ° C |
cm/cm/°C | ASTM E831 | |
|
垂直 -40.0~40°C Vertical -40.0~40 ° C |
cm/cm/°C | ASTM E831 | |
|
导热系数 Thermal conductivity coefficient |
|||
|
|
W/m/K | ISO 8032 | |
|
|
W/m/K | ASTM D5930 | |
|
球压测试 Ball pressure test |
℃ | IEC 60695-10-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
|
ohms·cm | IEC 60093 | |
|
|
ohms·cm | ASTM D257 | |
|
表面电阻率 Surface resistivity |
|||
|
|
ohms | IEC 60093 | |
|
|
ohms | ASTM D257 | |
|
绝缘强度 Insulation strength |
|||
|
0.80mm在油中 0.80mm in oil |
kV/mm | IEC 60243 | |
|
3.2mm在油中 3.2mm in oil |
kV/mm | IEC 60243 | |
|
1.6mm在空气中 1.6mm in air |
kV/mm | IEC 60243 | |
|
3 .2mm在空气中 3.2mm in air |
kV/mm | IEC 60243 | |
|
介电常数 Dielectric constant |
|||
|
50/60Hz 50/60Hz |
IEC 60250 | ||
|
1MHz 1MHz |
IEC 60250 | ||
|
50/60Hz 50/60Hz |
ASTM D150 | ||
|
1MHz 1MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
50/60Hz 50/60Hz |
IEC 60250 | ||
|
1MHz 1MHz |
IEC 60250 | ||
|
50/60Hz 50/60Hz |
ASTM D150 | ||
|
1MHz 1MHz |
ASTM D150 | ||
|
CTI CTI |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.5mm 1.5mm |
UL 94 | ||
|
2.5mm 2.5mm |
UL 94 | ||
|
2.5mm 2.5mm |
UL 94 | ||
|
1.0mm 1.0mm |
UL 94 | ||
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
1.5mm 1.5mm |
℃ | IEC 60695 | |
|
3.0mm 3.0mm |
℃ | IEC 60695 | |
|
1.0mm 1.0mm |
℃ | IEC 60695 | |
|
2.0mm 2.0mm |
℃ | IEC 60695 | |
|
灼热丝相对温度 Relative temperature of heating wire |
|||
|
1.5mm 1.5mm |
℃ | IEC 60695 | |
|
3.0mm 3.0mm |
℃ | IEC 60695 | |
|
2.0mm 2.0mm |
℃ | IEC 60695 | |
|
1.0mm 1.0mm |
℃ | IEC 60695 | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部 
美国原油价格跃升至2013年以来最高点
2022-03-04 据CNBC网站3月2日消息 在周二的夜间交易中，美国原油价格攀升至2013年以来的最高水平。随着原油价格持续飙升，全球基准布伦特原油价格突破每桶110美元。这一进展正值欧佩克及其石 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |