牌号简介 About |
---|
此材料的状态为“商业:限量发行”。此材料的数据最近尚未验证。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.10 到 0.30 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.1 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
10300 | MPa | ASTM D638 |
拉伸强度 tensile strength |
158 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
自然橡胶全球创新研发中心在海南成立
2017-11-21 天然橡胶全球创新研发中心18日在海南博鳌成立,拟通过加强创新,为天然橡胶产业发展创造新市场空间,深化天然橡胶多领域国际合作。 在当天举行的第五届国际天然橡胶产业(博鳌)论坛上,中国天然橡胶协会、国际橡胶研究组织、泰国橡胶局、海南天然橡胶产业集团股份有限公司及合盛农业集团公司签署了战略文件,共同发起成立天然橡胶全球创新研发中心。 农业部对外经济合作中心主任杨易在论坛上表示,我国是全球天然橡胶第一大消费国和第一大进口国,2016年需求量约489.6万吨,占世界消 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |