牌号简介 About |
---|
BJB的F-1系列,工作时间为3到10分钟,满足了缩短加工时间和提高零件生产的需要。这些5-95肖氏A产品具有优良的物理性能,在室温下易于加工。您也会发现简单的混合比是非常方便和墨盒分配友好。对于较长的工作时间,考虑我们的M系列或L系列弹性体。.符合RoHS/Reach标准,适用于零件和模具,高拉伸强度和撕裂强度,特殊效果和道具,易于着色。 BJB's "F-1 Series", with its 3 to 10 minutes of work time, addresses the need for shorter processing times and higher part production. These 5-95 Shore A products exhibit excellent physical properties and easily process at room temperature. You'll also find the easy mix ratio to be extremely convenient and cartridge dispense friendly. For longer work times consider our M Series or L Series of elastomers. . RoHS/REACH Compliant Popular for Parts & Molds High Tensile & Tear Strengths Special Effects & Props Over Molding Easy to Pigment |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 2 |
1.02 | g/cm³ | |
-- -- |
1.06 | g/cm³ | ASTM D792 |
-- -- 3 |
1.10 | g/cm³ | |
特定体积 Specific volume |
0.954 | cm³/g | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
6.51 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
25℃ 25℃ |
wk | ||
热固性混合粘度 Thermosetting mixed viscosity |
|||
25℃ 25℃ 4 |
cP | ||
25℃ 25℃ 5 |
cP | ||
25℃ 25℃ 6 |
cP | ||
脱模时间 stripping time |
|||
25℃ 25℃ |
min | ||
胶凝时间 Gelation time |
min | ||
工作时间 working hours 7 |
|||
25℃ 25℃ 7 |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
25℃ 25℃ |
day | ||
|
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D412 |
备注 |
---|
2. Part B, 77°F |
3. Part A, 77°F |
4. Part A |
5. Part B |
6. Mixed |
7. 100g mass |
【新闻资讯】查看全部
模具硬度缺乏、硬度不均的原因及对策剖析
2017-03-01 模具热处理硬度是非常重要的力学性能指标,硬度不合格是十分严重的缺陷。模具热处理后硬度不足或硬度不均将使模具耐磨性及疲劳强度等性能降低,导致模具早起失效,严重降低模具的使用寿命。 1.产生原因 1)模具截面大,钢材淬透性差,如大型模具选用了淬透性低的钢种。 2)模具钢原始组织中碳化物偏析严重或组织粗大,钢中存在石墨碳和碳化物偏析、聚集。 3)模具锻造工艺不正确,锻造后未进行很好的球化退火,使模具钢球化组织不良。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |