| 牌号简介 About |
|---|
| 福特斯3D生产系统的生产级热塑性塑料ABS-M30I是一种高强度材料，非常适合医疗、制药和食品包装行业。用ABS-M30I材料制造的零件具有生物相容性（ISO 10993 USP第六类），可以进行γ或ETO灭菌。当与Fortus 3D生产系统相结合时，ABS-M30i为您提供具有良好机械性能的生物相容性真实零件，这些零件非常适合概念建模、功能原型、制造工具和最终用途零件。 Production-Grade Thermoplastic for Fortus 3D Production Systems ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 USP Class VI) and can be gamma or EtO sterilized. When combined with Fortus® 3D Production Systems, ABS-M30i gives you biocompatible Real Parts™ with excellent mechanical properties that are well suited for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. |
产品描述 Product Description
用途：医疗/护理用品;工程配件;成型材料;医疗器械;药物;包装;食品包装;成型;药品包装;
颜色：象牙色
加工条件：3D Printing, Fused Filament Fabrication (FFF)
性能特点： 防火阻燃等级HB; 机械强度好; 经久耐用; 耐化学性; 耐高温; 生物兼容性; 辐射消毒; 环氧乙烷消毒; 冲击性能好; Good Rigidity,High impact resistance,Biocompatible,High Heat Resistance,Radiation disinfection,Durability,Solvent resistance,Ethylene oxide disinfection,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.04 | g/cm³ | ASTM D792 |
|
Thickness（Layer Capability） Thickness（Layer Capability） |
127.0 到 330.2 | µm | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
140 | J/m | ASTM D256-A |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
280 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
95.6 | ℃ | ASTM D648 |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
|
MD MD |
1/℃ | ASTM E831 | |
|
TD TD |
1/℃ | ASTM E831 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric strength 6 , 7 |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant 7 |
ASTM D150 | ||
|
耗散因数 Dissipation factor 7 |
ASTM D150 | ||
|
体积电阻 Volumetric resistance 7 |
ohms | ASTM D257 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
拉伸模量 Tensile modulus 3 |
|||
|
3.18 mm 3.18 mm 3 |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 3 |
|||
|
3.18 mm 3.18 mm 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂，3.18 mm Fracture, 3.18 mm 3 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 1, 0.20 in/min |
| 3 方法 I (三点负荷), 0.050 in/min |
| 4 标准 B (120°C/h), 载荷2 (50N) |
| 5 方法A（短时间） |
| 6 All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
|
【新闻资讯】查看全部
超实用的增加塑料制件膨胀方案
2016-03-22 对于表面质量要求很高的大型家电精密塑料模具制品，收缩(缩水)是个大难题。这是塑料模具加工商们面临的大敌，为此人们开发了各种技术，以最大限度地减少收缩，提高产品尺寸稳定和外观。 在塑料模具部件较厚位置，如筋肋(俗称骨位)突起处形成的收缩要比邻近位置更严重，这是由于较厚区域的冷却速度要比周围区域慢得多。冷却速度不同导致连接面处形成凹陷，即为人们所熟悉的收缩痕。形成收缩痕的原因可能有一个或多个，包括加工方法、部件几何形状、材料的选择以及模具设计等，其中几何形状和材料选择通常由原材 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付