PP均聚，ALTECH® PP-H A 2030/556 LE GF30 CP对比PP均聚，TRANSMARE® 10HGF30-0.001物性表,价格行情_搜料

牌号信息	ALTECH® PP-H A 2030/556 LE GF30 CP 物性表 PP均聚 & 德国爱彼斯指导价格：暂无塑料库存：缺货	TRANSMARE® 10HGF30-0.001 物性表 PP均聚 & 荷兰Transmare 指导价格：暂无塑料库存：缺货
牌号简介	ALTECH® PP-H A 2030/556 LE GF30 CP是一种聚丙烯均聚物(PP Homopoly)产品,含有的填充物为30% 玻璃纤维增强材料。它可以通过注射成型进行加工,在北美洲、欧洲或亚太地区有供货。典型应用领域为:汽车行业。特性包括: 通过 ROHS 认证低排放量化学耦合均聚物耐热 ALTECH® PP-H A 2030/556 LE GF30 CP is a Polypropylene Homopolymer (PP Homopolymer) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include: RoHS Compliant Chemically Coupled Heat Resistant Homopolymer Low Emissions	TRANSMARE® 10HGF30-0.001是一种30%化学耦合玻璃纤维增强聚丙烯均聚物。它结合了良好的冲击性能和高刚度，以及良好的流动性能。 TRANSMARE® 10HGF30-0.001 is a 30% chemically coupled glass fiber reinforced polypropylene homopolymer. It combines good impact properties with a high stiffness, and good flow properties.

产品描述
厂家：	德国爱彼斯 ALBIS	荷兰Transmare
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	玻璃纤维 30	玻璃纤维 30
用途：	汽车领域的应用
性能特点：	耐老化,易流动,低VOC,化学耦合,均聚物 Good heat aging resistance,Good liquidity,Low odor,Chemical coupling,Homopolymer	机械强度好,冲击性能好,可回收,易流动,化学耦合,均聚物 Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Chemical coupling,Homopolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL ALTECH® PP-H A 2030/556 LE GF30 CP TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL ALTECH® PP-H A 2030/556 LE GF30 CP TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，4 mm)
Tensile strain % ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂，4 mm)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(4 mm)
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT ALTECH® PP-H A 2030/556 LE GF30 CP TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-40℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(--)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-40℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁缺口冲击强度(--)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

热性能
THERMAL ALTECH® PP-H A 2030/556 LE GF30 CP TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

补充信息
ALTECH® PP-H A 2030/556 LE GF30 CP TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

Emission - of Volatile Organics
Emission - of Volatile Organics µgC/g Internal Method

加工方式

注射 ALTECH® PP-H A 2030/556 LE GF30 CP TRANSMARE® 10HGF30-0.001 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 - 除湿干燥剂 hr

干燥温度 - 除湿干燥剂 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 3-point

4 VW 50180, PV 3341


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
补充信息
加工方式
注射
备注
返回顶部