PA6，Durethan® BCF30XH3.0 901510 DUS040对比PA6，Durethan® BCF30XH3.0 000000物性表,价格行情_搜料

牌号信息	Durethan® BCF30XH3.0 901510 DUS040 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货	Durethan® BCF30XH3.0 000000 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	PA 6，30%玻璃纤维/碳纤维，注塑成型，热老化稳定，提高导电率 Durethan® BCF30XH3.0 901510 DUS040 (Dry) PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 901510 DUS040 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 901510 DUS040 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity	PA 6，30%玻璃纤维/碳纤维，注塑成型，热老化稳定，提高导电率 Durethan® BCF30XH3.0 000000 (Dry) PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 000000 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 000000 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维/碳纤维 30	玻璃纤维/碳纤维 30
用途：
性能特点：	热稳定性好,导电 Heat Stabilized,Conductive	导电,热稳定性好 Conductive,Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³

收缩率(MD：120℃，2.0 mm)
Shrinkage rate %

收缩率(MD：280℃，2.0 mm)
Shrinkage rate %

收缩率(TD：120℃，2.0 mm)
Shrinkage rate %

收缩率(TD：280℃，2.0 mm)
Shrinkage rate %

机械性能
MECHANICAL Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

拉伸应变(断裂，23℃)
Tensile strain %

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸模量(23℃)
Tensile modulus MPa

冲击性能
IMPACT Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量(-30℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

多轴向仪器化冲击能量(23℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

熔融温度
Melting temperature ℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃

电气性能
ELECTRICAL Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位
UNIT 测试方法
TEST METHOD

体积电阻率(23℃)
Volume resistivity ohms·cm

表面电阻率
Surface resistivity ohms

补充信息
Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

加工方式

注射 Durethan® BCF30XH3.0 901510 DUS040 Durethan® BCF30XH3.0 000000 单位测试方法

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

2. 60x60x2mm, 4 hr

3. 60x60x2mm, 80°C MT, 600 bar

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min

2. 60x60x2mm, 4 hr

3. 60x60x2mm, 80°C MT, 600 bar

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
补充信息
加工方式
注射
备注
返回顶部

PA6，Durethan® BCF30XH3.0 901510 DUS040对比PA6，Durethan® BCF30XH3.0 000000对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别