PC，LEXAN™ Copolymer CXT19UV对比PC，LEXAN™ Copolymer CXT19物性表,价格行情_搜料

牌号信息	LEXAN™ Copolymer CXT19UV 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ Copolymer CXT19 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Lexan CXT19UV树脂是一种紫外固化的高热聚碳酸酯共聚物树脂，VICAT为190°C，透明透明。该树脂经过优化，具有较宽的加工窗口和有限的黄变。它的透明色有限。 LEXAN™ CXT19UV Resin is an UV-stabilized High Heat Polycarbonate Copolymer Resin with Vicat of 190°C and crystal clear transparency. This resin is optimized to have a broad processing window with limited yellowing. It is available in limited transparent colors.	Lexan CXT19树脂是一种高温聚碳酸酯共聚物树脂，VICAT为190°C，透明透明。该树脂经过优化，具有较宽的加工窗口和有限的黄变。它的透明色有限。 LEXAN™ CXT19 Resin is a High Heat Polycarbonate Copolymer Resin with Vicat of 190°C and crystal clear transparency. This resin is optimized to have a broad processing window with limited yellowing. It is available in limited transparent colors.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	照明应用,汽车内部零件,Automotive Lighting,电子显示器,电器用具	照明应用,汽车内部零件,电子显示器,Automotive Lighting,电器用具
性能特点：	耐候抗UV Weather resistance is good
加工条件：

技术参数

物理性能
PHYSICAL LEXAN™ Copolymer CXT19UV LEXAN™ Copolymer CXT19 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(330℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(350℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体质量流动速率(330℃，2.16kg)
Melt Flow Rate g/10min

熔体质量流动速率(350℃，2.16kg)
Melt Flow Rate g/10min

机械性能
MECHANICAL LEXAN™ Copolymer CXT19UV LEXAN™ Copolymer CXT19 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ Copolymer CXT19UV LEXAN™ Copolymer CXT19 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL LEXAN™ Copolymer CXT19UV LEXAN™ Copolymer CXT19 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

玻璃化转变温度(一半的宽度)
Glass transition temperature ℃ 内部方法

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

光学性能
OPTICAL LEXAN™ Copolymer CXT19UV LEXAN™ Copolymer CXT19 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ISO 489

色散系数
Dispersion coefficient ISO 489

透光率(1000 µm)
Transmittance %

透光率(2000 µm)
Transmittance %

透光率(3000 µm)
Transmittance %

加工方式

注射 LEXAN™ Copolymer CXT19UV LEXAN™ Copolymer CXT19 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

2. 5.0 mm/min

3. 类型 1, 50 mm/min

4. 1.3 mm/min

5. 2.0 mm/min

6. at Yield

7. 80*10*3 sp=62mm

8. 80*10*3 mm

9. 80*10*4 mm

10. 标准 B (120°C/h), 载荷2 (50N)