LDPE，Lutene® LB7500对比LDPE，TAISOX 6634F物性表,价格行情_搜料

牌号信息	Lutene® LB7500 物性表 LDPE & 韩国LG化学指导价格：暂无塑料库存：缺货	TAISOX 6634F 物性表 LDPE & 台湾台塑指导价格：暂无塑料库存：缺货
牌号简介	鲁特尼LB7500主要用于挤压涂层，可以加工均匀的厚度和宽度。鲁特尼LB7500还以优异的热稳定性和良好的硅涂层加工性能而闻名。LB7500与纸和纸板具有良好的粘合强度和优良的颈部特性。叶黄素LB7500不含添加剂。 LUTENE LB7500 is mainly intended for extrusion coating and can be processed uniform thickness and width. LUTENE LB7500 is also noted for the excellent heat stability and has good silicone coating processibility. LB7500 has a good adhesion strength with paper and paper board and excellent neck-in characteristic. LUTENE LB7500 contains no additives.	TAISOX 6634F是一种低密度聚乙烯材料,。加工方式为:注射成型。 TAISOX 6634F的主要特性有: Antiblock 软件高流动性滑动坚硬 TAISOX 6634F的典型应用领域为:薄膜 TAISOX® 6634F is a Low Density Polyethylene material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of TAISOX® 6634F are: Antiblock High Flow Rigid Slip Typical application of TAISOX® 6634F: Film

产品描述
厂家：	韩国LG化学 LG Chemical	台湾台塑 fpc-tw
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	涂层应用,包装,层压板	薄膜
性能特点：	易加工,内缩量低,粘结性好 Excellent Processability,Low shrinkage,Good bond	高光滑性,流动性高,低密度 Smoothness,High liquidity,Low density
加工条件：	挤出涂层	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Lutene® LB7500 TAISOX 6634F 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
Lutene® LB7500 TAISOX 6634F 单位
UNIT 测试方法
TEST METHOD

割线模量(1% 正割，MD：30 µm，吹塑薄膜)
Secant modulus MPa ASTM D882

割线模量(1% 正割，TD：30 µm，吹塑薄膜)
Secant modulus MPa ASTM D882

埃尔曼多夫抗撕强度(MD：30 µm，吹塑薄膜)
Elmandorf tear strength g ASTM D1922

埃尔曼多夫抗撕强度(TD：30 µm，吹塑薄膜)
Elmandorf tear strength g ASTM D1922

拉伸应变(MD，断裂，30 µm，吹塑薄膜)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，30 µm，吹塑薄膜)
Tensile strain % ASTM D882

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(MD，屈服，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

水蒸气渗透性(25℃)
water vapor permeability MPa ASTM D393

落锤冲击(30 µm，吹塑薄膜)
Drop hammer impact g ASTM D1709

薄膜厚度
film thickness

薄膜厚度(测试)
film thickness µm

热性能
THERMAL Lutene® LB7500 TAISOX 6634F 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃

熔融温度
Melting temperature ℃ DSC

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

脆化温度
Embrittlement temperature ℃ ASTM D746

机械性能
MECHANICAL Lutene® LB7500 TAISOX 6634F 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(模压成型)
Bending modulus MPa ASTM D790

拉伸应变(断裂，模压成型)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂，模压成型)
tensile strength MPa ASTM D638

摩擦系数(吹塑薄膜)
friction coefficient ASTM D1894

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，模压成型)
Shore hardness ASTM D2240

光学性能
OPTICAL Lutene® LB7500 TAISOX 6634F 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，30 µm，吹塑薄膜)
gloss ASTM D2457

雾度(30 µm，吹塑薄膜)
Haze % ASTM D1003

备注

1 一般属性：这些不能被视为规格。

2 1 atm

1 一般属性：这些不能被视为规格。