PP，SABIC® PP 95610对比PP，Borealis PP KSR4525物性表,价格行情_搜料

牌号信息	SABIC® PP 95610 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Borealis PP KSR4525 物性表 PP & 奥地利北欧化工指导价格：暂无塑料库存：缺货
牌号简介	SABIC® PP 95610是一种反应器弹性体改性材料，具有优异的抗冷冲击性能。它是一种非常有吸引力的替代非填充化合物，常用于汽车保险杠。SABIC® PP 95610是指定的汽车等级。 SABIC® PP 95610 is a reactor-elastomer-modified material which offers an excellent cold impact resistance. It is a highly attractive alternative to non-filled compounds and is commonly used for car bumpers. SABIC® PP 95610 is a designated automotive grade.	KSR4525是一种反应器弹性体改性聚丙烯，用于注塑成型。本产品为天然色。这种材料具有良好的平衡力学性能，表面质量良好。 KSR4525 is a reactor elastomer modified polypropylene intended for injection moulding. The product is available in natural colour. This material has excellent balanced mechanical properties and gives a good surface quality. Applications KSR4525 has been developed especially for the car industry to be used in automotive exterior parts. Bumpers Exterior trims Special Features UV stabilised

产品描述
厂家：	沙特沙伯基础 SABIC	奥地利北欧化工 Borealis AG
类别：	PP PP not specified	PP PP not specified
填料：
用途：	汽车防撞杆,汽车领域的应用	汽车防撞杆,汽车外部装饰
性能特点：	冲击性能好,耐低温冲击 High impact resistance,low-temperature impact resistance	耐候抗UV,可回收 Weather resistance is good,Renewable resources
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SABIC® PP 95610 Borealis PP KSR4525 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(24 hrs)
Shrinkage rate %

收缩率(MD：24 hrs)
Shrinkage rate %

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT SABIC® PP 95610 Borealis PP KSR4525 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-20℃，注塑成型)
Impact strength of cantilever beam notch ASTM D256-A

悬臂梁缺口冲击强度(-20℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃，注塑成型)
Impact strength of cantilever beam notch ASTM D256-A，ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch ASTM D256-A，ISO 180-1A

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(0℃，注塑成型)
Charpy Notched Impact Strength

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength

热性能
THERMAL SABIC® PP 95610 Borealis PP KSR4525 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD：-30~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525，ISO 306/A120 4 4

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/B

维卡软化温度(B120)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B120 5 5

机械性能
MECHANICAL SABIC® PP 95610 Borealis PP KSR4525 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(屈服，注塑成型)
Tensile strain % ASTM D638

拉伸应变(屈服，注塑成型)
Tensile strain % ISO 527-2/1A/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，注塑成型)
tensile strength MPa ASTM D638

拉伸强度(屈服，注塑成型)
tensile strength MPa ISO 527-2/1A/50

拉伸模量(1 mm)
Tensile modulus MPa ISO 527-2

拉伸模量(1% 正割，注塑成型)
Tensile modulus MPa ASTM D638

拉伸模量(注塑成型)
Tensile modulus MPa ISO 527-2/1A/1

球压硬度
Ball hardness MPa ISO 2039-1

邵氏硬度(邵氏 D)
Shore hardness ISO 868

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 2.0 in/min

4 标准 B (120°C/h), 压力1 (10N)

5 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 0.079 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
备注
返回顶部

PP，SABIC® PP 95610对比PP，Borealis PP KSR4525对比物性表,价格行情_搜料_soliao