PC，LEXAN™ Copolymer LUX9132C对比PC，LEXAN™ Copolymer LUX9136C物性表,价格行情_搜料

牌号信息	LEXAN™ Copolymer LUX9132C 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ Copolymer LUX9136C 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Lexan Lux9132C聚碳酸酯（PC）树脂是一种无填充、注塑成型的等级。这种非氯化、非溴化阻燃PC具有1.5 mm的UL-94V0额定值，高流动能力，并且紫外线稳定，提供额外的风化能力。Lexan Lux9132C提供扩散色。 LEXAN LUX9132C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and is UV stabilized providing additional weathering capability. LEXAN LUX9132C is available in diffusion colors.	Lexan Lux9136C聚碳酸酯（PC）树脂是一种无填充、注塑成型的等级。这种非氯化、非溴化阻燃PC具有1.5 mm的UL-94V0额定值，高流动能力，并且紫外线稳定，提供额外的风化能力。Lexan Lux9136C提供扩散色。 LEXAN LUX9136C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and is UV stabilized providing additional weathering capability. LEXAN LUX9136C is available in diffusion colors.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	照明应用,电子显示器,电气/电子应用领域	照明应用,电气/电子应用领域
性能特点：	耐候抗UV,无卤,阻燃 Weather resistance is good,Halogen free,Flame Characteristics	耐候抗UV,无卤,阻燃 Weather resistance is good,Halogen free,Flame Characteristics
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

室外适用性
Outdoor applicability UL 746C

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(123~127℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 11

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位
UNIT 测试方法
TEST METHOD

介电常数(1.10 GHz)
Dielectric constant ASTM ES7-83

耗散因数(1.1 GHz)
Dissipation factor ASTM ES7-83

阻燃性能
FLAMMABILITY LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.5 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1.5 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(0.40 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

加工方式

注射 LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注射说明 LEXAN™ Copolymer LUX9132C LEXAN™ Copolymer LUX9136C 单位测试方法

备注

3. 50 mm/min

4. 类型 1, 50 mm/min

5. 1.3 mm/min

6. 2.0 mm/min

7. at Yield

8. 80*10*3 sp=62mm

9. 80*10*3 mm

10. 120*10*4 mm

11. 速率 A (50°C/h), 载荷2 (50N)