PC，LEXAN™ Copolymer FST9405T对比PC，LEXAN™ Copolymer FST9405物性表,价格行情_搜料

牌号信息	LEXAN™ Copolymer FST9405T 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ Copolymer FST9405 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LexanFST9405T树脂是一种高流动性PC共聚物树脂，适用于注塑成型。这种无卤阻燃树脂符合OSU55/55和FAR25.583标准，是飞机内部应用的理想选择。提供不透明颜色。 Lexan FST9405T resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.583 compliant and an ideal candidate foraircraft interior applications. Available in opaque colors.	LexanFST9405树脂是一种高流动性PC共聚物树脂，适用于注塑成型。这种无卤阻燃树脂符合OSU55/55和FAR25.583标准，是飞机内部应用的理想选择。提供不透明颜色。 Lexan FST9405 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.583 compliant and an ideal candidate foraircraft interior applications. Available in opaque colors.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	航空航天应用	航空航天应用
性能特点：	流动性高,无卤,阻燃,共聚物 High liquidity,Halogen free,Flame Characteristics,Copolymer	流动性高,无卤,阻燃,共聚物 High liquidity,Halogen free,Flame Characteristics,Copolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ Copolymer FST9405T LEXAN™ Copolymer FST9405 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate %

收缩率(TD)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ Copolymer FST9405T LEXAN™ Copolymer FST9405 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ Copolymer FST9405T LEXAN™ Copolymer FST9405 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ Copolymer FST9405T LEXAN™ Copolymer FST9405 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

阻燃性能
FLAMMABILITY LEXAN™ Copolymer FST9405T LEXAN™ Copolymer FST9405 单位
UNIT 测试方法
TEST METHOD

NBS烟雾密度(Flaming，Dmax)
NBS smoke density ASTM E662

OSU峰值放热速率(5 minute test)
OSU peak heat release rate (5 minute test) kW/m² FAR 25.853

OSU总放热量(2 minute test)
OSU total heat release (2 minute test) kW·min/m² FAR 25.853

垂直燃烧测试(a，60s，passes at)
Vertical combustion test sec FAR 25.853

加工方式

注射 LEXAN™ Copolymer FST9405T LEXAN™ Copolymer FST9405 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

2. 5.0 mm/min

3. 类型 1, 50 mm/min

4. 1.3 mm/min

5. 2.0 mm/min

6. at Yield

7. 80*10*3 sp=62mm

8. 80*10*4 mm

9. 80*10*3 mm

10. 速率 A (50°C/h), 载荷2 (50N)