PBT，POCAN® B3235HRLT 904040对比PBT，POCAN® B3235LT 904040物性表,价格行情_搜料

牌号信息	POCAN® B3235HRLT 904040 物性表 PBT & 德国恩骅力指导价格：暂无塑料库存：缺货	POCAN® B3235LT 904040 物性表 PBT & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	PBT，30%玻璃纤维，注塑，提高激光透明度，提高焊接性，水解稳定，近红外激光透明着色（黑色） POCAN® B3235HRLT 904040 PBT, 30 % glass fibers, injection molding, improved laser-transparency, improved weldability, hydrolysis stabilized, NIR-laser transparent coloring (black) POCAN® B3235HRLT 904040 PBT, 30 % glass fibers, injection molding, improved laser-transparency, improved weldability, hydrolysis stabilized, NIR-laser transparent coloring (black) POCAN® B3235HRLT 904040 PBT, 30 % glass fibers, injection molding, improved laser-transparency, improved weldability, hydrolysis stabilized, NIR-laser transparent coloring (black)	PBT，30%玻璃纤维，注塑成型，提高激光透明度，近红外激光透明着色（黑色） POCAN® B3235LT 904040 PBT, 30 % glass fibers, injection molding, improved laser-transparency, NIR-laser transparent coloring (black) POCAN® B3235LT 904040 PBT, 30 % glass fibers, injection molding, improved laser-transparency, NIR-laser transparent coloring (black) POCAN® B3235LT 904040 PBT, 30 % glass fibers, injection molding, improved laser-transparency, NIR-laser transparent coloring (black)

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：	玻璃纤维 30	玻璃纤维 30
用途：
性能特点：	焊接,耐水解 Welding,Hydrolysis stability
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(2.0 mm)
Shrinkage rate %

收缩率(MD：120℃，2.0 mm)
Shrinkage rate %

收缩率(MD：2.0 mm)
Shrinkage rate %

收缩率(TD：120℃，2.0 mm)
Shrinkage rate %

收缩率(TD：2.0 mm)
Shrinkage rate %

熔体体积流动速率(270℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178/A

弯曲强度(23℃)
bending strength MPa ISO 178-A

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

热性能
THERMAL POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

补充信息
POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

加工方式

注射 POCAN® B3235HRLT 904040 POCAN® B3235LT 904040 单位测试方法

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - 除湿干燥剂 hr

干燥温度 - 除湿干燥剂 °C

模具温度 °C

备注

2. 60x60x2mm

3. 60x60x2mm, 4 hr

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min

3. 60x60x2mm

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
补充信息
加工方式
注射
备注
返回顶部