技术参数
机械性能 MECHANICAL
NORYL PPO EN140
Hepla® H2018CM
单位 UNIT
测试方法 TEST METHOD
107.8
107.8
ISO 178
110.5
110.5
ASTM D790
2.0 mm/min
2.0 mm/min
2.8
2.8
ASTM D638
4.2
4.2
ASTM D638
5.0 mm/min
5.0 mm/min
50.0 mm Span, 1.3 mm/min
50.0 mm Span, 1.3 mm/min
70.2
70.2
ASTM D638
71
71
ASTM D638
Flexural Modulus, 2.0 mm/min
Flexural Modulus, 2.0 mm/min
MPa
ISO 178
Flexural Stress, break
Flexural Stress, break
Flexural Stress, yield
Flexural Stress, yield
Tensile Modulus, 5.0 mm/min
Tensile Modulus, 5.0 mm/min
MPa
ASTM D638
Tensile Strain, break, Type I
Tensile Strain, break, Type I
Tensile Strain, yield, Type I
Tensile Strain, yield, Type I
Tensile Stress, break, Type I
Tensile Stress, break, Type I
Tensile Stress, yield, Type I
Tensile Stress, yield, Type I
弯曲强度(屈服,2 mm/min)
bending strength
MPa
ISO 178
弯曲模量(50.0 mm Span, 1.3 mm/min)
Bending modulus
MPa
ASTM D790
抗张程度,50 mm/min(屈服)
Tensile strength, 50 mm/min
MPa
ISO 527
抗张程度,50 mm/min(断裂)
Tensile strength, 50 mm/min
MPa
ISO 527
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/5
拉伸应变(屈服,50 mm/min)
Tensile strain
%
ISO 527
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/5
拉伸应变(断裂,50 mm/min)
Tensile strain
%
ISO 527
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/5
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/5
拉伸模量
Tensile modulus
MPa
ISO 527-2/1
拉伸模量(1 mm/min)
Tensile modulus
MPa
ISO 527
冲击性能 IMPACT
NORYL PPO EN140
Hepla® H2018CM
单位 UNIT
测试方法 TEST METHOD
Notched Izod Impact, -30℃
Notched Izod Impact, -30℃
J/m
ASTM D256
悬臂梁无缺口冲击强度(80*10*4, -30℃)
Notched impact strength of cantilever beam
kJ/m2
ISO 180/1U
悬臂梁无缺口冲击强度(80*10*4, 23℃)
Notched impact strength of cantilever beam
kJ/m2
ISO 180/1U
悬臂梁缺口冲击强度, 23℃
Impact strength of cantilever beam notch, 23 ℃
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃,80*10*4)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(80*10*4 -30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(80*10*4, -30)
Impact strength of cantilever beam notch
kJ/m2
ISO 180/1A
悬臂梁缺口冲击强度(80*10*4, 23℃)
Impact strength of cantilever beam notch
kJ/m2
ISO 180/1A
简支梁无缺口冲击强度(80*10*4, -30℃)
Charpy Unnotch Impact strength
kJ/m2
ISO 179/1eU
简支梁无缺口冲击强度(80*10*4, 23℃)
Charpy Unnotch Impact strength
kJ/m2
ISO 179/1eU
简支梁缺口冲击强度(80*10*4, -30℃)
Charpy Notched Impact Strength
kJ/m2
ISO 179/1eA
简支梁缺口冲击强度(80*10*4, 23℃)
Charpy Notched Impact Strength
kJ/m2
ISO 179/1eA
飞镖冲击强度(23℃, Total Energy)
Dart impact strength
J
ASTM D3763
热性能 THERMAL
NORYL PPO EN140
Hepla® H2018CM
单位 UNIT
测试方法 TEST METHOD
0.45MPa,未退火
0.45MPa, unannealed
210
℃
100mm Span, 120*10*4 mm
100mm Span, 120*10*4 mm
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/Be
热变形温度(0.45 MPa,未退火,100 mm跨距)
Hot deformation temperature
℃
ISO 75/Be
热变形温度(1.8 MPa,未退火,100 mm跨距)
Hot deformation temperature
℃
ISO 75/Ae
球压测试(125℃±2℃)
Ball pressure test
IEC 60695-10-2
线性热膨胀系数(Flow : -40 to 40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(Flow : 23 to 60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(MD:23~60℃)
Linear coefficient of thermal expansion
线性热膨胀系数(TD)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(Transverse : -40 to 40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(Transverse : 23 to 60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525
维卡软化温度(A50)
Vicat Softening Temp
℃
ISO 306
维卡软化温度(B120)
Vicat Softening Temp
℃
ISO 306
维卡软化温度(B50)
Vicat Softening Temp
℃
ISO 306
物理性能 PHYSICAL
NORYL PPO EN140
Hepla® H2018CM
单位 UNIT
测试方法 TEST METHOD
Moisture Absorption(Saturation, 23℃)
Moisture Absorption
%
ISO 62
Moisture Absorption(平衡,23℃, 50% RH)
Moisture Absorption
%
ISO 62
吸水率(平衡,23℃,50% RH)
Water absorption rate
%
ISO 62
吸水率(饱和,23℃)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
收缩率(MD)
Shrinkage rate
%
内部方法
收缩率(MD:3.20 mm)
Shrinkage rate
%
NFD Method
熔体体积流动速率((220℃/5.0 kg))
Melt Volume Rate
cm3 /10min
ISO 1133
熔体体积流动速率(280℃,5 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体质量流动速率((280℃/5.0 kg))
Melt Flow Rate
g/10 min
ASTM D1238
电气性能 ELECTRICAL
NORYL PPO EN140
Hepla® H2018CM
单位 UNIT
测试方法 TEST METHOD
体积电阻率
Volume resistivity
ohms•cm
NFD Method