PP均聚，INNOPOL® PP CS 1-7830 HGF对比PP均聚，TRANSMARE® 10HGF30-0.001物性表,价格行情_搜料

牌号信息	INNOPOL® PP CS 1-7830 HGF 物性表 PP均聚 & 匈牙利Inno-Comp 指导价格：暂无塑料库存：缺货	TRANSMARE® 10HGF30-0.001 物性表 PP均聚 & 荷兰Transmare 指导价格：暂无塑料库存：缺货
牌号简介	Innopol CS 1-7830 HGF是一种30%玻璃纤维填充聚丙烯均聚物化合物。该等级有自然色和定制色两种形式。推荐使用Innopol CS 1-7830 HGF，适用于除长期热稳定性外，所需性能为高强度和刚度的应用。 INNOPOL ® CS 1-7830 HGF is a 30 % glass-fibre-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 1-7830 HGF is recommended to be used for applications where the required properties are high strength and stiffness besides long term heat stability.	TRANSMARE® 10HGF30-0.001是一种30%化学耦合玻璃纤维增强聚丙烯均聚物。它结合了良好的冲击性能和高刚度，以及良好的流动性能。 TRANSMARE® 10HGF30-0.001 is a 30% chemically coupled glass fiber reinforced polypropylene homopolymer. It combines good impact properties with a high stiffness, and good flow properties.

产品描述
厂家：	匈牙利Inno-Comp	荷兰Transmare
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	玻璃纤维 30	玻璃纤维 30
用途：
性能特点：	机械强度好,热稳定性好,均聚物 Good Rigidity,Heat Stabilized,Homopolymer	机械强度好,冲击性能好,可回收,易流动,化学耦合,均聚物 Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Chemical coupling,Homopolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(注塑成型)
Bending modulus MPa ISO 178

拉伸应变(屈服，注塑成型)
Tensile strain %

拉伸应变(断裂，4 mm)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，注塑成型)
Tensile strain %

拉伸强度(屈服，注塑成型)
tensile strength MPa

拉伸强度(断裂，4 mm)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂，注塑成型)
tensile strength MPa

拉伸模量(4 mm)
Tensile modulus MPa ISO 527-1-2

拉伸模量(注塑成型)
Tensile modulus MPa ISO 527-2/2

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-40℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃，注塑成型)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-40℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁无缺口冲击强度(23℃，注塑成型)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃，注塑成型)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A120

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

补充信息
INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位
UNIT 测试方法
TEST METHOD

Emission - of Volatile Organics
Emission - of Volatile Organics µgC/g Internal Method

加工方式

注射 INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

注射说明 INNOPOL® PP CS 1-7830 HGF TRANSMARE® 10HGF30-0.001 单位测试方法

备注

2、2.0 mm/min

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 3-point

4 VW 50180, PV 3341


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
补充信息
加工方式
注射
注射说明
备注
返回顶部

PP均聚，INNOPOL® PP CS 1-7830 HGF对比PP均聚，TRANSMARE® 10HGF30-0.001对比物性表,价格行情_搜料_soliao