PA46，Stanyl® TQ300对比PA46，Stanyl® HGR2 BK00001物性表,价格行情_搜料

牌号信息	Stanyl® TQ300 物性表 PA46 & 德国恩骅力指导价格：暂无塑料库存：缺货	Stanyl® HGR2 BK00001 物性表 PA46 & 德国恩骅力指导价格：112717.5元/吨塑料库存： 5000kg
牌号简介	特点：热稳定或热稳定用于：正时链条张紧器表面，Stanyl是我们的高性能聚酰胺46，用于汽车、机电、齿轮和户外动力设备。锡基是一种高性能聚酰胺，在要求较高的耐热性、设计刚度、磨损和摩擦以及工艺流程质量的应用中提供无与伦比的性能和价值。由于锡基在高达220°C的高温下仍保持其机械性能，因此它非常适合高性能应用，其性能优于PPA、PA6T、PA9T，通常还优于PPS和LCP。 Special Features: Heat stabilized or stable to heat Used In: Timing Chain Tensioner Surfaces Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments. Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required. Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.	Stanyl® HGR2 BK00001是一种聚酰胺 46（尼龙 46）材料,。该产品在北美洲、欧洲或亚太地区有供货,。 Stanyl® HGR2 BK00001的主要特性有: 热稳定剂润滑 Stanyl® HGR2 BK00001是一种聚酰胺 46（尼龙 46）材料,。该产品在北美洲、欧洲或亚太地区有供货,。 Stanyl® HGR2 BK00001的主要特性有: 热稳定剂润滑

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PA46 PA 46	PA46 PA 46
填料：
用途：
性能特点：	热稳定性好 Heat Stabilized	热稳定性好,润滑性 Heat Stabilized,Lubricating
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Stanyl® TQ300 Stanyl® HGR2 BK00001 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ISO 294-4

粘数
Viscosity number cm³/g

机械性能
MECHANICAL Stanyl® TQ300 Stanyl® HGR2 BK00001 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa

弯曲模量(120℃)
Bending modulus MPa

弯曲模量(160℃)
Bending modulus MPa

拉伸应变(屈服)
Tensile strain %

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa

拉伸强度(屈服，120℃)
tensile strength MPa

拉伸强度(屈服，120℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，160℃)
tensile strength MPa

拉伸强度(屈服，160℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，180℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，200℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量(--)
Tensile modulus MPa

拉伸模量(--)
Tensile modulus MPa ISO 527-2

拉伸模量(120℃)
Tensile modulus MPa

拉伸模量(120℃)
Tensile modulus MPa ISO 527-2

拉伸模量(160℃)
Tensile modulus MPa

拉伸模量(160℃)
Tensile modulus MPa ISO 527-2

拉伸模量(180℃)
Tensile modulus MPa ISO 527-2

拉伸模量(200℃)
Tensile modulus MPa ISO 527-2

标称拉伸断裂应变
Nominal tensile fracture strain %

标称拉伸断裂应变(120℃)
Nominal tensile fracture strain % ISO 527-2

标称拉伸断裂应变(160℃)
Nominal tensile fracture strain % ISO 527-2

标称拉伸断裂应变(180℃)
Nominal tensile fracture strain % ISO 527-2

标称拉伸断裂应变(200℃)
Nominal tensile fracture strain % ISO 527-2

冲击性能
IMPACT Stanyl® TQ300 Stanyl® HGR2 BK00001 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Stanyl® TQ300 Stanyl® HGR2 BK00001 单位
UNIT 测试方法
TEST METHOD

温度指数(5000 hrs)
Temperature index ℃ IEC 60216

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃

熔融温度
Melting temperature ℃ ISO 11357-3

玻璃化转变温度
Glass transition temperature ℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃

加工方式

注射 Stanyl® TQ300 Stanyl® HGR2 BK00001 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

干燥温度 - 热风干燥机 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆压缩比

备注

2、10°C/min

1 一般属性：这些不能被视为规格。

2 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注