牌号信息
高亮区别 隐藏相同

POLIMAXX P702BK

HDPE & 泰国IRPC

DGDK-6862 NT

HDPE & 美国陶氏

单位
测试方法
物性对比 价格对比
高亮区别 隐藏相同
牌号信息

POLIMAXX P702BK 物性表

HDPE & 泰国IRPC

指导价格:暂无

塑料库存: 缺货

DGDK-6862 NT 物性表

HDPE & 美国陶氏

指导价格:暂无

塑料库存: 缺货

牌号简介 POLIMAXX P702BK是由高密度聚乙烯制成的特种护套化合物,用于光缆护套。POLIMAXX P702BK是挤出电线电缆护套的专用复合材料,具有耐磨、抗应力开裂、加工方便等特点。它含有专为挤压工艺设计的必要添加剂。因此,它将提供优良的抗紫外线和耐候性。 POLIMAXX P702BK is special jacket compound produced from High-Density Polyethylene used for sheath of optical fiber cable. POLIMAXX P702BK is special compound for the purpose of extruding wire and cable jacket, providing abrasion resistance, stress-cracking resistance and easy process ability. It contains necessary additives designed especially for extrusion process. Thus, it will provide excellent UV and weathering resistance.
      
应用于自着色的 Dow AXELERON™ GP K-6862 NT 聚乙烯树脂是一种高密度聚乙烯树脂,在适当着色、经过稳定化处理之后可作为电缆的护套材料。这种材料具有高硬度、韧性高、拉伸强度高,耐热性能更高,此外,它还具有良好的柔软性、优异的耐环境应力开裂性能和良好的加工性能。 由于其独特的HDPE 和 MDPE的性能组合使得 Dow AXELERON™ GP K-6862 NT 特别适宜于作为电力电缆和电信电缆的护套材料。 加工建议: Dow AXELERON™ GP K-6862 NT 的挤出加工可使用很多普通的带夹套挤出机。典型的挤出机料桶温度取决于很多因素,比如挤出机规格和机头尺寸等。一个较好的出发点是: 在熔融温度低于250°C时,挤出机料桶温度设置为140/190/200/200/200/210/210°C。 应用领域: Dow AXELERON™ GP K-6862 NT 是一种原色树脂,可与炭黑或者色母料共混并需加入一种合适的紫外线稳定剂以确保其具有足够的耐候性能。需要加入适量的抗氧剂以确保其长期的耐老化性能。 这些护套可用于电力电缆和电信电缆,包括光纤电缆。 储存: 储存环境和储存条件会极大地影响物料的储存时间。在极端条件下的储存有可能影响产品的质量、加工或者性能表现。应该按照良好制造规范来进行储存,比如储存环境干燥,储存温度在10 到 30°C之间。
 Dow™ Electrical & Telecommunications DGDK-6862 NT Polyethylene Resin for Self coloring Jackets is a high density Polyethylene resin that can be used as a cable jacketing material when properly colored and stabilized. The material exhibits properties such as high hardness, toughness, tensile strength and heat resistance in combination with good flexibility, excellent environmental stress crack resistance and good processing properties. Due to the unique combination of HDPE and MDPE properties, DGDK-6862 NT is an excellent material for power cable and telecommunications cable jackets. Applications. DGDK-6862 NT is a natural resin that needs to be blended with a carbon black or color masterbatch with a suitable U.V.-stabilizer to ensure sufficient weathering resistance. The addition of a suitable antioxidant level is required for ageing resistance. A carbon black masterbatch with extra antioxidant for use with DGDK-6862 NT is Dow™ Electrical & Telecommunications DFDK-6010 BK. The jacket can be used for power cables and telecommunication cables including fiber optic cables. Storage. The environment or conditions of storage greatly influences the recommended storage time. Storage under extreme conditions may affect the quality, processing or performance of the product. Storage should be in accordance with good manufacturing practices such as a dry environment and storage temperatures between 10 and 30°C. Main Characteristics: High Vicat softening point Good flexibility Excellent ESCR Low shrinkage Specifications. The polymeric material meets the following raw material specification(s): ASTM D 1248 Type III, Class A, Category 4, Grade J4 ISO 1872-PE, KGN, 40-D006 In combination with a proper carbon black or colour masterbatch cable jackets made of Dow™ Electrical and Telecommunications DGDK-6862 NT, using industry standard extrusion practices, should meet the following cable standards: EN 50290-2-24, grade HD IEC 60502 ST7 IEC 60840 ST7 HD 620 S2 Part 1, Table 4B, Compound DMP 2, 9, 10, 14, 15, 17 (black) and DMP 5, 13, 16, 18 (coloured) Consult the regulations for complete details.
      
产品描述
厂家: 泰国IRPC 美国陶氏 DOW
类别: HDPE   HDPE HDPE   HDPE   
填料:         
用途: 电线电缆应用,光纤电缆护套   电线电缆应用,同轴电缆护套材料     
性能特点: 耐候抗UV,易加工,机械强度好-撕裂,耐磨,高密度   Weather resistance is good,Excellent Processability,Good tear strength,Good wear resistance,High density      
加工条件: 挤出   Extrusion      
技术参数
物理性能
PHYSICAL
POLIMAXX P702BK DGDK-6862 NT 单位
UNIT
测试方法
TEST METHOD
密度
Density
g/cm³ ISO 1183
抗环境应力开裂
ESCR(Environmental Stress Cracking Resistance)
hr ASTM D1693
抗环境应力开裂(50 ℃,10%非离子表面活性剂,F0)
ESCR(Environmental Stress Cracking Resistance)
hr IEC 60811
收缩率
Shrinkage rate
% ISO 294-4
炭黑含量
Carbon black content
wt% ISO 6964
熔体质量流动速率(190℃,2.16kg)
Melt Flow Rate
g/10min ISO 1133
熔体质量流动速率(190℃,5.0kg)
Melt Flow Rate
g/10min ISO 1133
热性能
THERMAL
POLIMAXX P702BK DGDK-6862 NT 单位
UNIT
测试方法
TEST METHOD
结晶峰温度(DSC)
Crystallization peak temperature
ASTM D3418
维卡软化温度
Vicat Softening Temp
ASTM D1525
维卡软化温度(A50)
Vicat Softening Temp
ISO 306/A50
脆化温度
Embrittlement temperature
ASTM D3895
电气性能
ELECTRICAL
POLIMAXX P702BK DGDK-6862 NT 单位
UNIT
测试方法
TEST METHOD
介电常数(1 MHz)
Dielectric constant
  ASTM D150
介电常数(1 MHz)
Dielectric constant
  IEC 60250
体积电阻率
Volume resistivity
ohms·cm ASTM D257
体积电阻率(23℃)
Volume resistivity
ohms·cm IEC 60093
耗散因数
Dissipation factor
  ASTM D150
机械性能
MECHANICAL
POLIMAXX P702BK DGDK-6862 NT 单位
UNIT
测试方法
TEST METHOD
弯曲模量
Bending modulus
MPa ISO 178
拉伸应变(断裂)
Tensile strain
% IEC 60811-401
拉伸应变(断裂)
Tensile strain
% IEC 60811-501
拉伸应变(断裂)
Tensile strain
% ISO 527-2
拉伸强度
tensile strength
MPa IEC 60811-501
拉伸强度(屈服)
tensile strength
MPa ISO 527-2
邵氏硬度(邵氏 D)
Shore hardness
  ASTM D2240
邵氏硬度(邵氏 D,15 秒)
Shore hardness
  ISO 868
加工方式
挤出 POLIMAXX P702BK DGDK-6862 NT 单位 测试方法
熔体温度 °C
备注
1 一般属性:这些不能被视为规格。
2 After ageing 10 days @100°C (212°F)
3 Notched, F0
  • 返回顶部返回顶部

价格走势对比图

HDPE      POLIMAXX P702BK

HDPE      DGDK-6862 NT

开始时间:结束时间:   
【牌号齐全,内容全面】 全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情 【精准,及时,权威!】 专业团队挖掘行情信息,第一时间发布行情
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
目录
我要询价    客服热线:400-6700-720
型号 类别 厂家 产地 颜色 首期使用量 后期使用量 包装 交期 成型产品 操作
GP-525N GPPS VATAA土耳其地区 亚太地区
价格:    含税     不含税     付款方式:    留言:

单据状态:未提交

我要询价
客服热线:400-6700-720

前往询价车
选择牌号
牌号 类别 厂家
暂无数据
该牌号已存在对比列表中 请选择其他牌号进行对比

您现在是未登录状态,想查看完整信息

登录免费注册