PA66，Ultramid® D3WG12 HMG BK00102对比PA66，AKROMID® A3 GF 60 1 black (2395)物性表,价格行情_搜料

牌号信息	Ultramid® D3WG12 HMG BK00102 物性表 PA66 & 德国巴斯夫指导价格：57750.0元/吨塑料库存： 2050kg	AKROMID® A3 GF 60 1 black (2395) 物性表 PA66 & 德国AKRO-PLASTIC 指导价格：暂无塑料库存：缺货
牌号简介	Ultramid® D3WG12 HMG BK00102是一种60%玻璃纤维增强，注塑成型聚酰胺提供高强度和刚度。由于固有的较低的吸湿性，Ultramid® D3WG12 HMG BK00102显示在湿度调节后机械性能的保持有所改善。此外，模具零件具有特殊的表面光洁度。应用程序Ultramid® D3WG12 HMG BK00102设计用于要求极高刚度的应用程序，应考虑使用金属制成的组件。 Ultramid D3WG12 HMG BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid D3WG12 HMG BK00102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish. Applications Ultramid D3WG12 HMG BK00102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.	AKROMID® A3 GF 60 1 black (2395)是一种60%玻璃纤维增强和热稳定的聚酰胺6.6，具有极高的刚性和强度，UL认证。应用主要是机械工程和汽车工业中的部件。进一步的应用是挤压绝缘型材。 AKROMID® A3 GF 60 1 black (2395) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength, UL listed. Components in mechanical engineering and in the automotive industry. Further application is extrusion of insulating profile.

产品描述
厂家：	德国巴斯夫 BASF	德国AKRO-PLASTIC
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 60	玻璃纤维 60
用途：	金属取代	工程配件,机器/机械部件,汽车领域的应用
性能特点：	机械强度好,表面光泽度好 Good Rigidity,Good surface appearance	机械强度好,热稳定性好,防火阻燃等级HB Good Rigidity,Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

吸水率(70℃，62% RH )
Water absorption rate % ISO 1110

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ISO 294-4

螺旋流动长度
Spiral flow length cm Internal Method

机械性能
MECHANICAL Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain %

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa

球压硬度(H 961/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ DIN EN 11357-1

熔融温度(DSC)
Melting temperature ℃

电气性能
ELECTRICAL Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

燃烧速率(1 mm)
Burning rate mm/min FMVSS 302

补充信息
Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位
UNIT 测试方法
TEST METHOD

灰份含量
Ash Content % ISO 1172

加工方式

注射 Ultramid® D3WG12 HMG BK00102 AKROMID® A3 GF 60 1 black (2395) 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 模具温度: 212°F, 熔体温度: 608°F, 注塑压力: 1.09E+4 psi

3 cross section of flow spiral: 7 mm x 3.5 mm

4 0.079 in/min

5 10°C/min

6 >1 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注