牌号信息	IROGRAN® A 92 K 4107 物性表 TPU-Capro & 美国亨斯迈指导价格：暂无塑料库存：缺货	IROGRAN® A 95 K 4640 物性表 TPU-Capro & 美国亨斯迈指导价格：暂无塑料库存：缺货
牌号简介	iRogran A92K 4107是一种基于己内酯的热塑性聚氨酯。该材料已开发用于注射成型应用，要求在压缩永久变形、耐磨性和抗水解性能方面优于传统的聚酯基TPU。iRogran A92K 4107是高性能注塑产品系列的一部分，提供一种特殊设计的柔性材料，适用于生产密封件、车轮和辊、耦合半轴和O形圈。性能特点：高耐磨性、低压缩永久变形、短循环时间、优异的抗水解性、高动态负荷 IROGRAN A92K 4107 is a caprolactone-based thermoplastic polyurethane. The material has been developed for injection molding applications requiring exceptional performance in terms of compression set, wear resistance and hydrolysis resistance over conventional polyester-based TPUs. IROGRAN A92K 4107 is part of the High Performance Injection Molding product range and offers a specially designed, flexible material suitable for the production of seals, wheels and rollers, coupling halfs and o-rings. PERFORMANCE FEATURES High wear resistance Low compression set Short cycle times Excellent hydrolysis resistance Resistant to high dynamic loads	iRogran A95K 4640是一种基于己内酯的热塑性聚氨酯。该材料已开发用于注射成型应用，要求在压缩永久变形、耐磨性和抗水解性能方面优于传统的聚酯基TPU。iRogran A95K 4640是高性能注塑产品系列的一部分，提供一种特殊设计的柔性材料，适用于生产密封件、车轮和辊、耦合半轴和O形圈。性能特点：高耐磨性、低压缩永久变形、短循环时间、优异的抗水解性、高动态负荷 IROGRAN A95K 4640 is a caprolactone-based thermoplastic polyurethane. The material has been developed for injection molding applications requiring exceptional performance in terms of compression set, wear resistance and hydrolysis resistance over conventional polyester-based TPUs. IROGRAN A95K 4640 is part of the High Performance Injection Molding product range and offers a specially designed, flexible material suitable for the production of seals, wheels and rollers, coupling halfs and o-rings. PERFORMANCE FEATURES High wear resistance Low compression set Short cycle times Excellent hydrolysis resistance Resistant to high dynamic loads

产品描述
厂家：	美国亨斯迈 Huntsman	美国亨斯迈 Huntsman
类别：	TPU-Capro TPU-Capro	TPU-Capro TPU-Capro
填料：
用途：	密封件,垫圈,滚轴,车轮	车轮,滚轴,密封件,垫圈
性能特点：	韧性好,尺寸稳定性好,耐水解,成型周期快,耐磨 Good flexibility,Good Dimensional Stability,Hydrolysis stability,Quick molding cycle,Good wear resistance	韧性好,尺寸稳定性好,耐水解,成型周期快,耐磨 Good flexibility,Good Dimensional Stability,Hydrolysis stability,Quick molding cycle,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL IROGRAN® A 92 K 4107 IROGRAN® A 95 K 4640 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ DIN 53479

收缩率(MD：注塑成型)
Shrinkage rate % ASTM D972

熔体体积流动速率(210℃，2.16 kg)
Melt Volume Rate cm³/10min

机械性能
MECHANICAL IROGRAN® A 92 K 4107 IROGRAN® A 95 K 4640 单位
UNIT 测试方法
TEST METHOD

磨耗量(--)
Wear amount mm³ ASTM D395

磨耗量(--)
Wear amount mm³ DIN 53516

邵氏硬度(邵氏 A，注塑成型)
Shore hardness ASTM D2240

邵氏硬度(邵氏 A，注塑成型)
Shore hardness DIN 53505

邵氏硬度(邵氏 D，注塑成型)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，注塑成型)
Shore hardness DIN 53505

弹性体
ELASTOMER IROGRAN® A 92 K 4107 IROGRAN® A 95 K 4640 单位
UNIT 测试方法
TEST METHOD

压缩形变(100℃，24 hr)
Compression deformation % ASTM D395

压缩形变(100℃，24 hr)
Compression deformation % DIN 53517

压缩形变(100℃，70 hr)
Compression deformation % ASTM D395

压缩形变(100℃，70 hr)
Compression deformation % DIN 53517

压缩形变(23℃，24 hr)
Compression deformation % ASTM D395

压缩形变(23℃，24 hr)
Compression deformation % DIN 53517

压缩形变(23℃，70 hr)
Compression deformation % ASTM D395

压缩形变(23℃，70 hr)
Compression deformation % DIN 53517

压缩形变(70℃，24 hr)
Compression deformation % ASTM D395

压缩形变(70℃，24 hr)
Compression deformation % DIN 53517

拉伸应变(断裂)
Tensile strain % ASTM D412

拉伸应变(断裂)
Tensile strain % DIN 53504

拉伸强度(100% 应变)
tensile strength MPa ASTM D412

拉伸强度(100% 应变)
tensile strength MPa DIN 53504

拉伸强度(20% 应变)
tensile strength MPa ASTM D412

拉伸强度(20% 应变)
tensile strength MPa DIN 53504

拉伸强度(200% 应变)
tensile strength MPa ASTM D412

拉伸强度(200% 应变)
tensile strength MPa DIN 53504

拉伸强度(300% 应变)
tensile strength MPa ASTM D412

拉伸强度(300% 应变)
tensile strength MPa DIN 53504

拉伸强度(50% 应变)
tensile strength MPa ASTM D412

拉伸强度(50% 应变)
tensile strength MPa DIN 53504

拉伸强度(断裂)
tensile strength MPa ASTM D412

拉伸强度(断裂)
tensile strength MPa DIN 53504

撕裂强度
tear strength kN/m ASTM D624

撕裂强度
tear strength kN/m DIN 53515

热性能
THERMAL IROGRAN® A 92 K 4107 IROGRAN® A 95 K 4640 单位
UNIT 测试方法
TEST METHOD

维卡软化温度
Vicat Softening Temp ℃ DIN 53372

加工方式

注射 IROGRAN® A 92 K 4107 IROGRAN® A 95 K 4640 单位测试方法

Dew Point °C

射嘴温度 °C

干燥时间-- hr

干燥时间Hot Air Dryer hr

干燥温度-- °C

干燥温度Hot Air Dryer °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Injection Molded

1 一般属性：这些不能被视为规格。

2 Injection Molded