牌号信息	LNP™ LUBRICOMP™ DCP32 compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ STAT-KON™ DEL33EC compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP™ LUBRICOMP™DCP32化合物LNPLubricompDCP32是一种基于聚碳酸酯树脂的化合物，含有15%的聚四氟乙烯/硅酮、10%的碳纤维。这种材料的附加特性包括：导电、耐磨。也称为：LNP™ LUBRICOMP™DCL-4532产品重新订购名称：DCP32LNP Lubricomp DCP32 LNP™ LUBRICOMP™ DCP32 compound LNP* LUBRICOMP* DCP32 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DCL-4532 Product reorder name: DCP32 LNP™ LUBRICOMP™ DCP32 compound LNP LUBRICOMP DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DCL-4532 Product reorder name: DCP32	lnp stat-kon del33ec化合物lnp stat-kondel33ec是一种基于聚碳酸酯树脂的化合物，含有15%碳纤维、15%聚四氟乙烯。附加功能包括：清洁的复合系统，导电，耐磨，易于成型。也被称为：lnpstat-kon化合物DCL-4033 em-ccs产品重新订购名称：del33ec lnp stat-kon del33ec化合物lnp stat-kondel33ec是基于含碳纤维、聚四氟乙烯的聚碳酸酯树脂的化合物。这种材料的附加特性包括：清洁的配制系统。也称为：lnpstat-kon化合物DCL-4033 em ccs产品再订购名称：del33ec LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Clean Compounding System, Electrically Conductive, Wear Resistant, Easy Molding.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	PTFE/碳纤维 15:10	PTFE/碳纤维 15
用途：
性能特点：	导电,润滑性,耐磨 Conductive,Lubricating,Good wear resistance	易加工,导电,低离子含量,润滑性,耐磨 Excellent Processability,Conductive,Low (to None) Ion Content,Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ DCP32 compound LNP™ STAT-KON™ DEL33EC compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ DCP32 compound LNP™ STAT-KON™ DEL33EC compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ DCP32 compound LNP™ STAT-KON™ DEL33EC compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ DCP32 compound LNP™ STAT-KON™ DEL33EC compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL LNP™ LUBRICOMP™ DCP32 compound LNP™ STAT-KON™ DEL33EC compound 单位
UNIT 测试方法
TEST METHOD

表面电阻率
Surface resistivity ohms ASTM D257

加工方式

注射 LNP™ LUBRICOMP™ DCP32 compound LNP™ STAT-KON™ DEL33EC compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注