PA共聚，Durethan® BKV 215 H2.0 901510对比PA共聚，Durethan® BKV 215 H3.0 000000物性表,价格行情_搜料

牌号信息	Durethan® BKV 215 H2.0 901510 物性表 PA共聚 & 德国恩骅力指导价格：暂无塑料库存：缺货	Durethan® BKV 215 H3.0 000000 物性表 PA共聚 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Durethan® BKV 215 H2.0 901510 含有15%的玻璃纤维PA 6共聚物材料，用注射成型方式进行加工，具有良好的抗冲击性能和热老化稳定性。 Durethan® BKV215H2.0 901510 (Dry) PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H2.0 901510 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H2.0 901510 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized	Durethan®BKV215 H3.0 000000（干燥）PA 6-共聚物，15％玻璃纤维，注塑成型，改善冲击强度，热老化稳定 Durethan®BKV215 H3.0 000000 PA 6-共聚物，15％玻璃纤维，注塑成型，提高冲击强度，热老化稳定 Durethan® BKV215H3.0 000000 (Dry) PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H3.0 000000 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H3.0 000000 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PA共聚 PA Copolymer	PA共聚 PA Copolymer
填料：	玻璃纤维 15	玻璃纤维 15
用途：
性能特点：	防火阻燃等级HB,冲击性能好,热稳定性好,共聚物 HB,High impact resistance,Heat Stabilized,Copolymer	冲击性能好,热稳定性好,共聚物,防火阻燃等级HB High impact resistance,Heat Stabilized,Copolymer,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：120℃，2.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(MD：120℃，3.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(MD：280℃，2.0 mm)
Shrinkage rate % ISO 2577

收缩率(MD：280℃，3.0 mm)
Shrinkage rate % ISO 2577

收缩率(TD：120℃，2.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(TD：120℃，3.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(TD：280℃，2.0 mm)
Shrinkage rate % ISO 2577

收缩率(TD：280℃，3.0 mm)
Shrinkage rate % ISO 2577

表观密度
Apparent density g/cm³ ISO 60

冲击性能
IMPACT Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击能量(-30℃)
Multi axial instrumented impact energy J ISO 6603-2

多轴向仪器化冲击能量(23℃)
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

阻燃性能
FLAMMABILITY Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

补充信息
Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 1874

机械性能
MECHANICAL Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178/A

弯曲强度(23℃)
bending strength MPa ISO 178-A

弯曲强度(3.50% 应变，23℃)
bending strength MPa ISO 178-A

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

球压硬度
Ball hardness MPa ISO 2039-1

加工方式

注射 Durethan® BKV 215 H2.0 901510 Durethan® BKV 215 H3.0 000000 单位测试方法

Residual Moisture Content %

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 60x60x2mm, 80°C MT, 600 bar

3 60x60x2mm

4 0.079 in/min

5 2 mm/min

6 10°C/min

7 程序 A

1 一般属性：这些不能被视为规格。

2 150x105x3mm, 80°C MT, 400 bar

3 150x105x3mm

4 0.079 in/min

5 2 mm/min

6 10°C/min

7 程序 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
补充信息
机械性能
加工方式
注射
备注
返回顶部

PA共聚，Durethan® BKV 215 H2.0 901510对比PA共聚，Durethan® BKV 215 H3.0 000000对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别