PUR，BCC Products BX-31对比PUR，BCC Products BX-41物性表,价格行情_搜料

牌号信息	BCC Products BX-31 物性表 PUR & 美国BCC Products 指导价格：暂无塑料库存：缺货	BCC Products BX-41 物性表 PUR & 美国BCC Products 指导价格：暂无塑料库存：缺货
牌号简介	BX-31是一个由两部分组成的聚氨酯成型系统。BX-31混合100 ISO:97重量治愈（或1 pt-a ISO到1 pt-b体积治愈）并在室温下治愈。BX-31固化至低硬度，肖氏A 31±2，浅黄色橡胶。在室温固化3-4天后，获得最终性能。可通过加热（130-150°F，12-16小时）加速固化，但可获得稍硬的聚合物（34+/-2邵尔A），并可获得轻微收缩。应用程序BX-31用于制造包含中等咬边的母版模具。BX-31的物理性能使其非常适合制作详细的混凝土模具、模型和模板内衬。 BX-31 is a two-part polyurethane molding system. BX-31 is mixed 100 iso:97 curative by weight (or 1 Pt-A Iso to 1 Pt-B Curative by volume) and cures at room temperature. BX-31 cures to a low hardness, Shore A 31±2, light yellow rubber. Ultimate properties are obtained after 3-4 days of room temperature cure. Cure can be accelerated with heat (130-150°F for 12-16 hours) but a slightly harder polymer (34 +/- 2 Shore A) and slight shrinkage will be obtained. Applications BX-31 is used to make molds of masters that contain moderate undercuts. BX-31's physical properties make it ideal for making detailed concrete molds, patterns and formliners.	BX-41是一个由两部分组成的聚氨酯成型系统。BX-41按重量100:97混合（或1份A ISO至1份B按体积治愈）并在室温下固化。BX-41固化至中等硬度，肖氏A 41±2，薰衣草橡胶。在室温固化3-4天后，获得最终性能。可通过加热（130-150°F，12-16小时）加速固化，但可获得稍硬的聚合物（43+/-2邵尔A），并可获得轻微收缩。应用BX-41用于制造包含小底切的母版模具。BX-41的物理性能使其成为制作混凝土模板和模板内衬的理想材料。BX-41的配方是为了减少收缩。 BX-41 is a two-part polyurethane molding system. BX-41 is mixed 100:97 by weight (or 1 Part-A Iso to 1 Part-B Curative by volume) and cures at room temperature. BX-41 cures to a medium hardness, Shore A 41±2, lavender rubber. Ultimate properties are obtained after 3-4 days of room temperature cure. Cure can be accelerated with heat (130-150°F for 12-16 hours) but a slightly harder polymer (43 +/- 2 Shore A) and slight shrinkage will be obtained. Applications BX-41 is used to make molds of masters that contain minor undercuts. BX-41's physical properties make it ideal for making concrete patterns and formliners. BX-41 has been formulated to reduce shrinkage.

产品描述
厂家：	美国BCC Products	美国BCC Products
类别：	PUR PUR	PUR PUR
填料：
用途：	模具制造,模板	模板,模具制造
性能特点：	低硬度,室温固化 Low Hardness,Room Temperature Cure	室温固化 Room Temperature Cure
加工条件：