PPS，POTICON RFK423对比PPS，Fortron® 0214物性表,价格行情_搜料

牌号信息	POTICON RFK423 物性表 PPS & 日本大冢化学指导价格：暂无塑料库存：缺货	Fortron® 0214 物性表 PPS & 美国塞拉尼斯指导价格：暂无塑料库存：缺货
牌号简介	Poticon系列的特点是钛酸钾微填料与热塑性树脂复合，提供卓越的微增强和尺寸稳定性。这些化合物的优良表面光滑度限制了对向材料的摩擦，减少了磨损并允许无脂应用。此外，由于Poticon减少了对模具和金属模具的损坏，并提供了良好的可回收性，它还降低了加工成本。优势显微强化优越的摩擦滑动和磨损减少优秀的尺寸精度和表面光滑度高度可回收应用汽车零件（齿轮、轴承）LED反光片手表零件（齿轮、地平面）摄像头（图像稳定零件）滑动零件（齿轮、车轮轴承）摄像头模块零件电机零件（齿轮、轴承）RFK423特性：滑动 The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs. Advantages Microscopic reinforcement Superior friction sliding and wear reduction Excellent dimensional accuracy and surface smoothness Highly recyclable Applications Automotive Parts (gears, bearings) LED Reflectors Watch Parts (gears, ground plane) Camera (image stabilization parts) Sliding Parts (gears, wheel bearing) Camera Module Parts Motor Parts (cog-wheels, bearings) RFK423 Property: Slide	0214是一种未填充等级，具有良好的熔融强度。这一等级显示出良好的耐热性和耐化学性。它可以被挤压成多丝。由于流动和熔融强度的良好平衡，本产品偶尔用于注塑件。可用粉末（0214B1）、颗粒（0214P1）和结晶颗粒（0214C1）形式的标准品。 0214 is an unfilled grade exhibiting good melt strength. This grade demonstrates excellent heat and chemical resistance. It can be extruded to produce multi-filaments. Due to the excellent balance of flow and melt strength, this product is occasionally used for injection molding parts. Available standard in powder (0214B1), pellet (0214P1) and crystallized pellet (0214C1) form.

产品描述
厂家：	日本大冢化学 Otsuka	美国塞拉尼斯 Celanese
类别：	PPS PPS	PPS PPS
填料：
用途：	齿轮,LEDs,轴承,汽车领域的应用,相机应用	细丝
性能特点：	尺寸稳定性好,可回收,低摩擦系数 Good Dimensional Stability,Renewable resources,Low coefficient of friction	易流动,耐高温,熔体强度好,耐化学性 Good liquidity,High Heat Resistance,Good melt strength,Solvent resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL POTICON RFK423 Fortron® 0214 单位
UNIT 测试方法
TEST METHOD

Density of Melt
Density of Melt g/cm³ Internal Method

Specific Heat Capacity of Melt
Specific Heat Capacity of Melt J/kg/℃ Internal Method

吸水率(平衡)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

特定体积
Specific volume cm³/g ASTM D792

粘度
viscosity Pa·s Internal Method

冲击性能
IMPACT POTICON RFK423 Fortron® 0214 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

热性能
THERMAL POTICON RFK423 Fortron® 0214 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

机械性能
MECHANICAL POTICON RFK423 Fortron® 0214 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

摩擦系数(与钢 - 动态)
friction coefficient

摩擦系数(与钢 - 动态)
friction coefficient Internal Method

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ISO 2039-2

磨损量(--)
Wear amount 10^-3 mm³/N·km

磨损量(of counterpart)
Wear amount 10^-3 mm³/N·km

电气性能
ELECTRICAL POTICON RFK423 Fortron® 0214 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耐电弧性
Arc resistance sec ASTM D495

耗散因数(1 kHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

补充信息
POTICON RFK423 Fortron® 0214 单位
UNIT 测试方法
TEST METHOD

Temperature
Temperature ℃ Internal Method

加工方式

注射 POTICON RFK423 Fortron® 0214 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

备注

2、Surface pressure: 1MPa

3、Slipping velocity: 0.3m/sec

1 一般属性：这些不能被视为规格。

2 Break

3 10°C/min

4 方法A（短时间）


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
电气性能
补充信息
加工方式
注射
备注
返回顶部