技术参数
机械性能
MECHANICAL
LEXAN™ EM3110R resin
LEXAN™ EM3110 resin
单位
UNIT
测试方法
TEST METHOD
弯曲强度(屈服,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲模量(1.30 mm/min,50 mm跨距)
Bending modulus
MPa
ASTM D790
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂,I型,50 mm/min)
Tensile strain
%
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(断裂,I型,50 mm/min)
tensile strength
MPa
ASTM D638
冲击性能
IMPACT
LEXAN™ EM3110R resin
LEXAN™ EM3110 resin
单位
UNIT
测试方法
TEST METHOD
仪表冲击能量峰值(23℃)
Instrument impact energy peak
N.m
ASTM D 3763
悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch
J/m
悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
J/m
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃,6.4mm)
Impact strength of cantilever beam notch
J/m
悬臂梁缺口冲击强度(23℃,6.4mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
装有测量仪表的落镖冲击(23℃,Energy at Peak Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能
THERMAL
LEXAN™ EM3110R resin
LEXAN™ EM3110 resin
单位
UNIT
测试方法
TEST METHOD
热变形温度(0.45 MPa)
Hot deformation temperature
℃
ASTM D 648
热变形温度(0.45 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
热变形温度(1.8MPa)
Hot deformation temperature
℃
ASTM D 648
热变形温度(未退火,6.4 mm)
Hot deformation temperature
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
线性热膨胀系数(MD:-40~95℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
物理性能
PHYSICAL
LEXAN™ EM3110R resin
LEXAN™ EM3110 resin
单位
UNIT
测试方法
TEST METHOD
吸水率(24hr)
Water absorption rate
%
ASTM D570
密度
Density
ASTM D792
密度
Density
g/cm³
ASTM D792
收缩率
Shrinkage rate
%
内部方法
收缩率(MD:3.2 mm)
Shrinkage rate
%
内部方法
熔体质量流动速率(300℃,1.20kg)
Melt Flow Rate
g/10min
ASTM D1238
阻燃性能
FLAMMABILITY
LEXAN™ EM3110R resin
LEXAN™ EM3110 resin
单位
UNIT
测试方法
TEST METHOD
1.47 mm
1.47 mm
UL 94