PP均聚，Braskem PP H 503对比PP均聚，TOTAL Polypropylene PPH 4069物性表,价格行情_搜料

牌号信息	Braskem PP H 503 物性表 PP均聚 & 巴西布拉斯科指导价格：暂无塑料库存：缺货	TOTAL Polypropylene PPH 4069 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	说明：H 503是一种低熔融流速均聚物，具有通用添加剂包装。设计用于注塑、拉菲亚挤出、生物定向膜和一般挤出。该产品具有优良的加工性能、良好的熔融稳定性、良好的刚度/冲击强度平衡和低气味和风味转移。应用：翻盖和可密封的封口；厚壁部件；家用电器；工业袋；大袋；复合材料；鸟类和农业用窗帘和覆盖物；绳索用单丝；渔网；船用电缆；牙刷和扫帚用刷毛。 H 503 is a low melt flow rate additivated homopolymer used for general purposes. It is designed for injection molding, raffia extrusion, bioriented film and general extrusion. This product exhibits excellent processability, good melt stability, good stiffness/impact strength balance and low odor and flavor transfer. Applications: Flip-top and resealable closures; Thick wall parts; Domestic appliances; Industrial bags; Big bags; Compounds; Curtains and covers to aviary and agriculture; Monofilament for ropes; Fishing nets; Cables for boats; Bristles for tooth brushes and brooms. Processing: Injection Moulding Raffia Extrusion Fiber Extrusion	聚丙烯PPH 4069是熔融流动指数为4 g/10 min的均聚物。聚丙烯PPH 4069用于挤压非织造布用高强度短纤维。它具有优良的纺纱性能。聚丙烯PPH 4069具有防气体褪色配方，可减少纤维变黄。 Polypropylene PPH 4069 is homopolymer with a Melt Flow Index of 4 g/10 min. Polypropylene PPH 4069 is intended for extrusion of high tenacity staple fibres for nonwoven applications. It exhibits excellent spinning properties. Polypropylene PPH 4069 has an anti gas-fading formulation to reduce yellowing in fibres.

产品描述
厂家：	巴西布拉斯科 Braskem	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	食品包装,薄膜,铠装电缆,绳索,厚壁配件（部件）,外壳,家用货品,农业应用,袋子,容器	无纺布,短纤维
性能特点：	机械强度好,易加工,冲击性能好,低透气性,无毒,均聚物,熔体稳定性高 Good Rigidity,Excellent Processability,High impact resistance,Low odor,Nontoxicity,Homopolymer,Higher melt stability	耐化学性,均聚物 Solvent resistance,Homopolymer
加工条件：	注射成型 Injection Molding	纤维（纺纱）挤出

技术参数

物理性能
PHYSICAL Braskem PP H 503 TOTAL Polypropylene PPH 4069 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

冲击性能
IMPACT Braskem PP H 503 TOTAL Polypropylene PPH 4069 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Braskem PP H 503 TOTAL Polypropylene PPH 4069 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，注塑成型)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，注塑)
Hot deformation temperature ℃ ASTM D648

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 3

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL Braskem PP H 503 TOTAL Polypropylene PPH 4069 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(1% 正割，注塑成型)
Bending modulus MPa ASTM D790

弯曲模量(1% 正割，注塑成型)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服，注塑成型)
Tensile strain % ASTM D638

拉伸应变(屈服，注塑成型)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服，注塑成型)
tensile strength MPa ASTM D638

拉伸强度(屈服，注塑成型)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

备注

1 一般属性：这些不能被视为规格。

2 压力1 (10N)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
备注