PAI，Torlon® 5030对比PAI，Duratron® T5530物性表,价格行情_搜料

牌号信息	Torlon® 5030 物性表 PAI & 比利时索尔维指导价格：暂无塑料库存： 3000kg	Duratron® T5530 物性表 PAI & 瑞士跨骏指导价格：暂无塑料库存：缺货
牌号简介	Torlon® 5030是一种30%玻璃纤维增强级聚酰胺-酰亚胺（PAI）树脂。它具有很高的强度和模量，以及优异的抗蠕变性能。它具有与铝相似的热膨胀特性，因此具有良好的尺寸稳定性。Torlon Pai具有最高强度和刚度的热塑性塑料高达275°C（525°F）。它具有优异的耐磨性、抗蠕变性和耐化学腐蚀性。Torlon® 5030树脂的机械性能使其成为高温、高应力应用中金属替代的候选材料。此外，它还具有优异的电气性能，是连接器、开关和继电器等高性能部件的理想选择。高流量：Torlon® 5030-HF低流量：Torlon® 5030-LF挤出等级：Torlon® 5030-E Torlon® 5030 is a 30% glass-fiber reinforced grade of polyamide-imide (PAI) resin. It offers high strength and modulus and exceptional creep resistance. It has thermal expansion characteristics similar to aluminum and therefore excellent dimensional stability. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep and chemicals. The mechanical properties of Torlon® 5030 resin make it a candidate for metal replacement in high temperature, high stress applications. In addition, it offers outstanding electrical properties, which makes it ideal for high performance parts such as connectors, switches and relays. High Flow: Torlon® 5030-HF Low Flow: Torlon® 5030-LF Extrusion Grade: Torlon® 5030-E	Duratron® T5530是30%玻璃增强，压缩成型的PAI。它是高负荷结构或电子应用的理想选择。该等级在成分上与Duratron T5030 PAI相似。当需要最大程度的尺寸控制时，可选择较大的形状。Duratron PLA是性能最高的熔融加工塑料。它对高温有很好的抵抗力。它能够在连续温度为500°F（260°C）的严重应力条件下工作。与大多数先进的工程塑料相比，用Duratron PLA材料制成的零件具有更高的压缩强度和抗冲击性。其极低的线性热膨胀系数和高的蠕变阻力在其整个使用范围内提供了良好的尺寸稳定性。Duratron聚乳酸是一种非晶材料，玻璃化转变温度为537°F（280°C）。象限工程塑料产品从象限EPP生产的库存形状和零件的测试中提供的数据。 Duratron® T5530 is a Polyamide-imide (PAI) product filled with glass fiber. It can be processed by compression molding and is available in Latin America or North America. Primary characteristic: flame rated.

产品描述
厂家：	比利时索尔维 Solvay	瑞士跨骏 Quadrant
类别：	PAI PAI	PAI PAI
填料：	玻璃纤维 30	玻璃纤维 30
用途：	电气元件,商务设备,金属取代,开关,汽车领域的应用,外壳,航空航天应用,飞机应用,电器外壳,电气/电子应用领域,机器/机械部件,石油/天然气用品,工业应用,工业部件,连接器,阀门/阀门部件,密封装置	电气/电子应用领域,构件
性能特点：	机械强度好,韧性好,尺寸稳定性好,阻燃,耐高温,抗压性能好,耐化学性 Good Rigidity,Good flexibility,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Good compressive strength,Solvent resistance	机械强度好,韧性好,冲击性能好,尺寸稳定性好,耐酒精,耐酸,耐磨,抗压性能好,耐化学性,热稳定性好,耐碳氢化合物,无定形的,防火阻燃等级V-0 Good Rigidity,Good flexibility,High impact resistance,Good Dimensional Stability,Ethanol tolerance,Acidproof,Good wear resistance,Good compressive strength,Solvent resistance,Heat Stabilized,Hydrocarbons,Amorphous,V-0
加工条件：	型材挤出成型 Profile extrusion	压缩模塑

技术参数

物理性能
PHYSICAL Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

压缩强度(10% 应变)
compressive strength MPa ASTM D695

压缩模量
Compression modulus MPa ASTM D695

弯曲强度(232℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(232℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D1708

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D1708

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(极限)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

摩擦系数(与钢 - 静态)
friction coefficient 内部方法

洛氏硬度(E 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ASTM D785

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

冲击性能
IMPACT Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256-A

热性能
THERMAL Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

导热系数
Thermal conductivity coefficient W/m/K ASTM F433

最高使用温度(Long Term，Air)
Maximum operating temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

玻璃化转变温度
Glass transition temperature ℃ ASTM D3418

线性热膨胀系数
Linear coefficient of thermal expansion cm/cm/℃ ASTM D696

线性热膨胀系数(MD：-40~149℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

电气性能
ELECTRICAL Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电常数(60 Hz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(60 Hz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms 内部方法

阻燃性能
FLAMMABILITY Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

阻燃等级(3.20 mm)
Flame retardant level UL 94

补充信息
Torlon® 5030 Duratron® T5530 单位
UNIT 测试方法
TEST METHOD

限压速度
Pressure limiting speed MPa·m/s 内部方法

加工方式

注射 Torlon® 5030 Duratron® T5530 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

螺杆长径比

备注

1 一般属性：这些不能被视为规格。

2 以前，ASTM标准试验方法D1708用于测量PAI和类似材料的拉伸性能，因为小试样能节约材料。现在使用最广泛的是ASTM D638 1 Bar 试样。所含D1708数值仅用作历史参考，不与D638值作对照用。

1 一般属性：这些不能被视为规格。

2 68°F

3 EOS/ESD S11.11

4 方法A（短时间）

5 4:1 safety factor


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

PAI，Torlon® 5030对比PAI，Duratron® T5530对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别