PEEK，KetaSpire® KT-880SFP对比PEEK，LUVOCOM® 1105-7106 VP物性表,价格行情_搜料

牌号信息	KetaSpire® KT-880SFP 物性表 PEEK & 比利时索尔维指导价格：暂无塑料库存：缺货	LUVOCOM® 1105-7106 VP 物性表 PEEK & 德国莱曼雷孚斯指导价格：暂无塑料库存：缺货
牌号简介	LUVOCOM® 1-7956 VP是一种聚酰胺66（尼龙66）材料,含有的填充物为碳纤维增强材料。该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1-7956 VP的主要特性有: 传导性良好的刚度典型应用领域包括: 工程/工业配件纺织/纤维汽车行业商业/办公用品 KetaSpire® KT-880SFP is the high flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color super-fine powder form. This super-fine PEEK powder is suitable for water borne coatings, electrostatically driven powder coatings, and resin pre-impregnation of continuous fiber composites. This super-fine powder is produced to a median particle size D50 of about 30 micrometers. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent chemical resistance to acids, bases and a broad range of aggressive organic chemicals, best in class fatigue resistance, high thermal resistance, high purity and ease of melt processing. These properties make KT-880SFP well-suited for applications in health care, transportation, electronics, chemical processing and other industrial uses. The resin is also available in a natural-colored pellet form under the grade name KT-880 NT for injection molding applications.	LUVOCOM® 1105-7106 VP是一种聚醚醚酮(PEEK)材料,含有的填充物为碳纤维增强材料。该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1105-7106 VP的主要特性有: 阻燃/额定火焰 Flame Retardant 良好的尺寸稳定性耐化学品耐磨典型应用领域包括: 工程/工业配件纺织/纤维航空航天汽车行业医疗/保健 LUVOCOM® 1105-7106 VP is a Polyetheretherketone (PEEK) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® 1105-7106 VP are: Flame Rated Chemical Resistant Flame Retardant Heat Resistant High Dimensional Stability Typical applications include: Engineering/Industrial Parts Aerospace Automotive Fabrics/Fibers Medical/Healthcare

产品描述
厂家：	比利时索尔维 Solvay	德国莱曼雷孚斯 Lehmann
类别：	PEEK PEEK	PEEK PEEK
填料：	碳纤维	碳纤维
用途：	凸轮,工程配件,纺织应用,商务设备,汽车领域的应用,齿轮	泵件,工程配件,航空航天应用,医疗/护理用品,纺织应用,衬套,汽车领域的应用,齿轮,轴承
性能特点：	机械强度好,导电 Good Rigidity,Conductive	尺寸稳定性好,耐水解,低摩擦系数,阻燃,自润滑,耐高温,润滑性,耐磨,耐化学性,防火阻燃等级V-0 Good Dimensional Stability,Hydrolysis stability,Low coefficient of friction,Flame Characteristics,Self-lubricating,High Heat Resistance,Lubricating,Good wear resistance,Solvent resistance,V-0
加工条件：

技术参数

物理性能
PHYSICAL KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate %

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % DIN 16901

熔体体积流动速率(380℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

颗粒大小(D50)
Particle size µm

颗粒大小(D90)
Particle size µm

颗粒大小(D99)
Particle size µm

机械性能
MECHANICAL KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位
UNIT 测试方法
TEST METHOD

最高使用温度(短期)
Maximum operating temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ASTM D3417

玻璃化转变温度
Glass transition temperature ℃ ASTM D3417

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ DIN 53752

线性热膨胀系数(MD：-50~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

连续使用温度
Continuous use temperature ℃ UL 746B

电气性能
ELECTRICAL KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位
UNIT 测试方法
TEST METHOD

绝缘电阻
insulation resistance ohms IEC 60167

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

加工方式

注射 KetaSpire® KT-880SFP LUVOCOM® 1105-7106 VP 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间

干燥温度

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

热风干燥机, A hr

热风干燥机, A °C

热风干燥机, B hr

热风干燥机, B °C

备注

1 一般属性：这些不能被视为规格。

2 Not recognized by UL.


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注