PC+ABS，EvoSource™ PC/ABS 5366 90/04对比PC+ABS，Cheng Yu C1100物性表,价格行情_搜料

牌号信息	EvoSource™ PC/ABS 5366 90/04 物性表 PC+ABS & 美国MBA Polymers 指导价格：暂无塑料库存：缺货	Cheng Yu C1100 物性表 PC+ABS & 香港成宇指导价格：暂无塑料库存：缺货
牌号简介	这是一种来自消费后来源的可回收PCabs，并针对需要改进性能的技术应用进行了改进：提高热偏转温度、改善冷冲击行为、改善不可燃性、提高缺口冲击强度。 This is a recycled PCABS from post-consumer sources and modified for technical applications demanding improved properties: Increased heat deflection temperature Improved cold impact behavior Improved non-flammability Increased notched impact strength	Cheng Yu C1100是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)产品,。它,在亚太地区有供货。特性包括: 阻燃/额定火焰耐冲击高流动性 Cheng Yu C1100 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific. Characteristics include: Flame Rated High Flow Impact Resistant

产品描述
厂家：	美国MBA Polymers	香港成宇 Cheng Yu
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：
用途：
性能特点：	冲击性能好,阻燃,耐高温,耐低温冲击,防火阻燃等级HB High impact resistance,Flame Characteristics,High Heat Resistance,low-temperature impact resistance,HB	冲击性能好,流动性高 High impact resistance,High liquidity
加工条件：	挤出 Extrusion

技术参数

物理性能
PHYSICAL EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位
UNIT 测试方法
TEST METHOD

吸水率
Water absorption rate % ISO 62

吸水率(饱和，23℃ )
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ 内部方法

收缩率(--)
Shrinkage rate % ISO 294-4

收缩率(48 hrs)
Shrinkage rate % ISO 294-4

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体质量流动速率
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(240℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服，2 mm/min，23℃)
bending strength MPa ISO 178

弯曲模量(2 mm/min，23℃)
Bending modulus MPa ISO 178

拉伸应变(50 mm/min，23℃)
Tensile strain % ISO 527-2

拉伸应变(屈服，23℃，50 mm/min)
Tensile strain % ISO 527-2

拉伸强度(23℃)
tensile strength MPa ISO 527-2/50

拉伸强度(23℃，50 mm/min )
tensile strength MPa ISO 527-2

拉伸强度(屈服，23℃，50 mm/min )
tensile strength MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃，1 mm/min )
Tensile modulus MPa ISO 527-2

泰伯磨耗试验
Taber abrasion test mg/1000 Cycles

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/A

热性能
THERMAL EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位
UNIT 测试方法
TEST METHOD

灼热丝相对温度(1.00mm)
Relative temperature of heating wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

电气性能
ELECTRICAL EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

介电常数(50-60 Hz)
Dielectric constant IEC 60250

体积电阻
Volumetric resistance Ω.cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

绝缘强度
Insulation strength KV/mm IEC 60243-1

绝缘强度(0.800mm，油中)
Insulation strength KV/mm IEC 60243-1

绝缘强度(1.60mm，油中)
Insulation strength KV/mm IEC 60243-1

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(50-60 Hz)
Dissipation factor IEC 60250

表面电阻
Surface resistance Ω.cm IEC 60093

加工方式

注射 EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

挤出 EvoSource™ PC/ABS 5366 90/04 Cheng Yu C1100 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
挤出
备注