PC，OmniCarb™ PC 120对比PC，LEXAN™ EXL1162T resin物性表,价格行情_搜料

牌号信息	OmniCarb™ PC 120 物性表 PC & 美国OMNI 指导价格：暂无塑料库存：缺货	LEXAN™ EXL1162T resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	易流动聚碳酸酯 Easy Flow, Polycarbonate	LEXAN EXL1162T聚碳酸酯（PC）硅氧烷共聚物树脂是一种透明注塑（IM）级树脂，具有额外的释放性能。与标准PC树脂相比，该树脂具有良好的低温（20 C）延展性、高流动性和良好的加工性，有机会缩短IM循环时间。LEXAN™ EXL1162T resin是一种通用产品，可提供透明和不透明的颜色，可能是广泛应用的最佳候选。 LEXAN EXL1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. LEXAN EXL1162T resin is a general purpose product available in transparent and opaque colors and may be an excellent candidate for a broad range of applications.

产品描述
厂家：	美国OMNI	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：
性能特点：	易流动,防火阻燃等级HB Good liquidity,HB	易加工,流动性高,机械强度好-延展,成型周期快,含脱模剂,共聚物,防火阻燃等级HB Excellent Processability,High liquidity,Ductility,Quick molding cycle,Good stripping performance,Copolymer,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792 , ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

洛氏硬度(L 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(强度机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~95℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~95℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525 11 , ISO 306/B50 11

阻燃性能
FLAMMABILITY OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(0.8 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

电气性能
ELECTRICAL OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

光学性能
OPTICAL OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位
UNIT 测试方法
TEST METHOD

透光率(2540 µm)
Transmittance % ASTM D1003

雾度(2540 µm)
Haze % ASTM D1003

加工方式

注射 OmniCarb™ PC 120 LEXAN™ EXL1162T resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 80*10*4 mm

10 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
光学性能
加工方式
注射
备注
返回顶部

PC，OmniCarb™ PC 120对比PC，LEXAN™ EXL1162T resin对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别