牌号信息	Sindustris ABS LXG680 物性表 ABS & 澳大利亚Sincerity 指导价格：暂无塑料库存：缺货	Sindustris ABS LXG679 物性表 ABS & 澳大利亚Sincerity 指导价格：暂无塑料库存：缺货
牌号简介	Sindustris ABS LXG680是一种丙烯腈丁二烯苯乙烯(ABS)材料,。该产品在亚太地区有供货,加工方式为:注射成型。 Sindustris ABS LXG680的主要特性有: 阻燃/额定火焰高流动性耐冲击耐划伤性典型应用领域包括: 房屋电气/电子应用。 Sindustris ABS LXG680 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LXG680 are: Flame Rated High Flow Impact Resistant Scratch Resistant Typical applications include: Housings Electrical/Electronic Applications	Sindustris ABS LXG679是一种丙烯腈丁二烯苯乙烯(ABS)材料,。加工方式为:注射成型。 Sindustris ABS LXG679的主要特性有: 阻燃/额定火焰高光泽度高流动性耐划伤性典型应用领域包括: 房屋电气/电子应用 Sindustris ABS LXG679 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LXG679 are: Flame Rated High Flow High Gloss Scratch Resistant Typical applications include: Housings Electrical/Electronic Applications

产品描述
厂家：	澳大利亚Sincerity	澳大利亚Sincerity
类别：	ABS ABS	ABS ABS
填料：
用途：	外壳,电器外壳,LCD 应用	电器外壳,LCD 应用,电视外壳
性能特点：	冲击性能好,流动性高,耐刮擦,防火阻燃等级HB High impact resistance,High liquidity,High scratch resistance,HB	表面光泽度好,流动性高,耐刮擦,防火阻燃等级HB Good surface appearance,High liquidity,High scratch resistance,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Sindustris ABS LXG680 Sindustris ABS LXG679 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Sindustris ABS LXG680 Sindustris ABS LXG679 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-20℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Sindustris ABS LXG680 Sindustris ABS LXG679 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

阻燃性能
FLAMMABILITY Sindustris ABS LXG680 Sindustris ABS LXG679 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

机械性能
MECHANICAL Sindustris ABS LXG680 Sindustris ABS LXG679 单位
UNIT 测试方法
TEST METHOD

弯曲强度(3.20 mm)
bending strength MPa ASTM D790

弯曲模量(3.20 mm)
Bending modulus MPa ASTM D790

拉伸应变(屈服，3.20 mm)
Tensile strain % ASTM D638

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(屈服，3.20 mm)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

补充信息
Sindustris ABS LXG680 Sindustris ABS LXG679 单位
UNIT 测试方法
TEST METHOD

耐臭氧性(5 sec)
Ozone resistance JIS K6301

加工方式

注射 Sindustris ABS LXG680 Sindustris ABS LXG679 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.59 in/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.59 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
机械性能
补充信息
加工方式
注射
备注
返回顶部

ABS，Sindustris ABS LXG680对比ABS，Sindustris ABS LXG679对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别