牌号信息	Lutene® LB5000 物性表 LDPE & 韩国LG化学指导价格：暂无塑料库存：缺货	TAISOX 6534F 物性表 LDPE & 台湾台塑指导价格：暂无塑料库存：缺货
牌号简介	鲁特尼LB5000主要用于挤压涂层，可以加工均匀的厚度和宽度。鲁特尼LB5000还以优异的热稳定性和良好的硅涂层加工性能而闻名。LB5000与纸和纸板具有良好的粘合强度和优良的颈部特性。叶黄素LB5000不含添加剂。机构评级：美国FDA 21CRF 117.1520（c）日本卫生福利部第20号通知标准应用：软包装（层压膜的粘结层或密封层）纸和纸板涂层（离型纸、纸杯、牛皮纸） LUTENE LB5000 is mainly intended for extrusion coating and can be processed uniform thickness and width. LUTENE LB5000 is also noted for the excellent heat stability and has good silicone coating processibility. LB5000 has a good adhesion strength with paper and paper board and excellent neck-in characteristic. LUTENE LB5000 contains no additives. Agency Ratings: USA FDA 21CRF 117.1520(c) Japaness Ministry of Health and Welfare Notification No. 20 Standard Applications: Flexible package (Tie layer or sealant layer of laminating film) Paper and paperboard coating (Release paper, paper cup, kraft paper)	TAISOX 6534F是一种低密度聚乙烯材料,。该产品在北美洲、欧洲或亚太地区有供货,。 TAISOX 6534F的主要特性有: Antiblock 软件滑动美观 TAISOX 6534F的典型应用领域为:电影 TAISOX® 6534F is a Low Density Polyethylene material. It is available in Asia Pacific, Europe, or North America. Important attributes of TAISOX® 6534F are: Antiblock Good Aesthetics Slip Typical application of TAISOX® 6534F: Film

产品描述
厂家：	韩国LG化学 LG Chemical	台湾台塑 fpc-tw
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	小袋 - 软包装,纸张涂料,层压板,涂层应用	薄膜
性能特点：	易加工,内缩量低,粘结性好 Excellent Processability,Low shrinkage,Good bond	高光滑性,易剥离,光学性能,低密度 Smoothness,Good dissection,Optical performance,Low density
加工条件：	层压法

技术参数

物理性能
PHYSICAL Lutene® LB5000 TAISOX 6534F 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
Lutene® LB5000 TAISOX 6534F 单位
UNIT 测试方法
TEST METHOD

割线模量(1% 正割，MD：30 µm，吹塑薄膜)
Secant modulus MPa ASTM D882

割线模量(1% 正割，TD：30 µm，吹塑薄膜)
Secant modulus MPa ASTM D882

埃尔曼多夫抗撕强度(MD：30 µm，吹塑薄膜)
Elmandorf tear strength g ASTM D1922

埃尔曼多夫抗撕强度(TD：30 µm，吹塑薄膜)
Elmandorf tear strength g ASTM D1922

始封温度
Initial sealing temperature ℃

拉伸应变(MD，断裂，30 µm，吹塑薄膜)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，30 µm，吹塑薄膜)
Tensile strain % ASTM D882

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(MD，屈服，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，30 µm，吹塑薄膜)
tensile strength MPa ASTM D882

水蒸气透过性
Water vapor permeability g/m²/24 hr 内部方法

落锤冲击(30 µm，吹塑薄膜)
Drop hammer impact g ASTM D1709

薄膜厚度
film thickness

薄膜厚度(测试)
film thickness µm

热性能
THERMAL Lutene® LB5000 TAISOX 6534F 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃

熔融温度
Melting temperature ℃ DSC

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

脆化温度
Embrittlement temperature ℃ ASTM D746

补充信息
Lutene® LB5000 TAISOX 6534F 单位
UNIT 测试方法
TEST METHOD

Adhesion to Aluminum
Adhesion to Aluminum N/m 内部方法

机械性能
MECHANICAL Lutene® LB5000 TAISOX 6534F 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(模压成型)
Bending modulus MPa ASTM D790

拉伸应变(断裂，模压成型)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂，模压成型)
tensile strength MPa ASTM D638

摩擦系数(吹塑薄膜)
friction coefficient ASTM D1894

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，模压成型)
Shore hardness ASTM D2240

光学性能
OPTICAL Lutene® LB5000 TAISOX 6534F 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，30 µm，吹塑薄膜)
gloss ASTM D2457

雾度(30 µm，吹塑薄膜)
Haze % ASTM D1003

加工方式

挤出 Lutene® LB5000 TAISOX 6534F 单位测试方法

内缩量 4 mm

最小涂层重量 5 g/m²

备注

1 一般属性：这些不能被视为规格。

2 Kraft paper, 40 g/m²

3 Coating weight: 40 g/m² (actually aluminum)

4 Coating speed: 200 m/min

5 Coating speed: 250 m/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
热性能
补充信息
机械性能
光学性能
加工方式
挤出
备注
返回顶部

LDPE，Lutene® LB5000对比LDPE，TAISOX 6534F对比物性表,价格行情_搜料_soliao