PA66，Leona™ 1300S对比PA66，Ultramid® A 205F NATURAL物性表,价格行情_搜料

牌号信息	Leona™ 1300S 物性表 PA66 & 日本旭化成指导价格：33075.0元/吨塑料库存： 46800kg	Ultramid® A 205F NATURAL 物性表 PA66 & 德国巴斯夫指导价格：26250.0元/吨塑料库存： 25800kg
牌号简介	Leona™ 1300S是一种聚酰胺66（尼龙66）产品,。它,在亚太地区、北美洲、欧洲或非洲和中东有供货。 Leona™ 1300S的应用领域包括工程/工业配件、汽车行业、生活消费品和电气/电子应用。特性包括: 阻燃/额定火焰良好的刚度良好的韧性 Leona™ 1300S is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 1300S include automotive, consumer goods, electrical/electronic applications and engineering/industrial parts. Characteristics include: Flame Rated Good Stiffness Good Toughness	Ultramid®A 205F Natural是一种用于注塑的无增强聚酰胺66。该等级具有两个主要优点：优异的填充质量和0.4 mm以下的UL 94 V2。它特别适合薄壁长零件的成型 TECHNYL® A 205F Natural is an unreinforced polyamide 66 for injection moulding. This grade offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly suitable for the moulding of long parts with thin wall sections

产品描述
厂家：	日本旭化成 Asahi Kasei	德国巴斯夫 BASF
类别：	PA66 PA66	PA66 PA66
填料：
用途：	汽车领域的应用,连接器,消费品应用领域,配件	薄壁部件,紧固件,连接器
性能特点：	机械强度好,韧性好,易流动 Good Rigidity,Good flexibility,Good liquidity	成型周期快,防火阻燃等级V-2,流动性高 Quick molding cycle,V-2,High liquidity
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Leona™ 1300S Ultramid® A 205F NATURAL 单位
UNIT 测试方法
TEST METHOD

吸水率 Water Absorption(24 h，23℃)
Water Absorption % ISO 62

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸湿性 Moisture Absorption(平衡，23℃。50%r.h.)
Moisture Absorption % ISO 62

密度
Density g/cm³ ASTM D792

密度 Density
Density kg/m³ ISO 1183

成型收缩率 Mold Shrinkage(平行 parallel)
Mold Shrinkage % ISO 294-4

成型收缩率 Mold Shrinkage(法向 normal)
Mold Shrinkage % ISO 294-4

收缩率(MD：2.0 mm)
Shrinkage rate % ASTM D995

收缩率(TD：2.0 mm)
Shrinkage rate % ASTM D995

热性能
THERMAL Leona™ 1300S Ultramid® A 205F NATURAL 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K JIS R2618

热变形温度 HDT(0.45 MPa)
Hot deformation temperature HDT ℃ ASTM D648

热变形温度 HDT(0.45 MPa)
Hot deformation temperature HDT ℃ ISO 75-1/-2

热变形温度 HDT(1.8 MPa)
Hot deformation temperature HDT ℃ ASTM D648

热变形温度 HDT(1.80 MPa)
Hot deformation temperature HDT ℃ ISO 75-1/-2

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度 Melting temperature
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(比热)
Linear coefficient of thermal expansion J/Kg/℃

电气性能
ELECTRICAL Leona™ 1300S Ultramid® A 205F NATURAL 单位
UNIT 测试方法
TEST METHOD

介电常数 Dielectric Constant(1 MHz)
Dielectric Constant IEC 62631-2-1

体积电阻率 Volume Resistivity(干燥 dry)
Volume Resistance ohm·m IEC 62631-3-1

体积电阻率 Volume Resistivity(湿润 cond.)
Volume Resistance ohm·m IEC 62631-3-1

相比漏电起痕指数 Comparative Tracking Index(测试液A，干燥 dry)
Compared Tracking Index IEC 60112

相比漏电起痕指数 Comparative Tracking Index(测试液A，湿润 cond.)
Compared Tracking Index IEC 60112

相比漏电起痕指数 Comparative Tracking Index(测试液B，干燥 dry)
Compared Tracking Index IEC 60112

绝缘强度()
Insulation strength KV/mm ASTM D149

耐电强度 Electric strength(d=0.8 mm)
Electric strength kV/mm IEC 60243-1

耐电强度 Electric strength(d=2.0 mm)
Electric strength kV/mm IEC 60243-1

耗散因数 Dissipation Factor(1 MHz)
Dissipation Factor E-4 IEC 62631-2-1

耗散因数(相比漏电起痕指数)
Dissipation factor V ASTM D3638

表面电阻率 Surface Resistivity(干燥 dry)
Surface Resistivity ohm IEC 62631-3-2

表面电阻率 Surface Resistivity(湿润 cond.)
Surface Resistivity ohm IEC 62631-3-2

阻燃性能
FLAMMABILITY Leona™ 1300S Ultramid® A 205F NATURAL 单位
UNIT 测试方法
TEST METHOD

极限氧指数 Oxygen Index
Oxygen Index % ISO 4589-2

灼热丝可燃性指数 Glow Wire Flammability Index(GWFI)(1.6 mm)
Glow Wire Flammability Index (GWFI) ℃ IEC 60695-2-12

阻燃等级 Flame Class Rating(0.4 mm)
Flame Class Rating calss IEC 60695-11-10

阻燃等级 Flame Class Rating(0.8 mm)
Flame Class Rating calss UL-94, IEC 60695

阻燃等级 Flame Class Rating(1.6 mm)
Flame Class Rating calss IEC 60695-11-10

阻燃等级 Flame Class Rating(3.2 mm)
Flame Class Rating calss UL-94, IEC 60695

阻燃等级(0.40mm)
Flame retardant level UL 94

阻燃等级(0.71mm)
Flame retardant level UL 94

阻燃等级(1.50mm)
Flame retardant level UL 94

阻燃等级(3.00mm)
Flame retardant level UL 94

阻燃等级(极限氧指数)
Flame retardant level % ASTM D2863

冲击性能
IMPACT Leona™ 1300S Ultramid® A 205F NATURAL 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度 Izod Notched Impact strength(干燥 dry)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度 Izod Notched Impact strength(干燥 dry)
Izod Notched Impact strength KJ/m² ISO 180/1A

悬臂梁缺口冲击强度 Izod Notched Impact strength(湿润 cond.)
Izod Notched Impact strength KJ/m² ISO 180/1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度 Charpy notched Impact strength(干燥 dry)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度 Charpy notched Impact strength(湿润 cond.)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

机械性能
MECHANICAL Leona™ 1300S Ultramid® A 205F NATURAL 单位
UNIT 测试方法
TEST METHOD

弯曲强度 Flexural Strength(干燥 dry)
Flexural Strength MPa ISO 178

弯曲强度 Flexural Strength(湿润 cond.)
Flexural Strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲模量 Flexural Modulus(干燥 dry)
Flexural Modulus MPa ASTM D790

弯曲模量 Flexural Modulus(干燥 dry)
Flexural Modulus MPa ISO 178

弯曲模量 Flexural Modulus(湿润 cond.)
Flexural Modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变 Tensile Strain(50 mm/min,干燥 dry)
Tensile Strain % ISO 527

拉伸应变 Tensile Strain(50 mm/min,湿润 cond.)
Tensile Strain % ISO 527

拉伸应变 Tensile Strain(断裂 brk，干燥 dry)
Tensile Strain % ISO 527

拉伸应变 Tensile Strain(断裂 brk，湿润 cond.)
Tensile Strain % ISO 527

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度 Tensile Strength(50 mm/min,干燥 dry)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(50 mm/min,湿润 cond.)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(屈服 yld，2 in/min，干燥 dry)
Tensile Strength MPa ASTM D638

拉伸强度 Tensile Strength(断裂 brk，干燥 dry)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(断裂 brk，湿润 cond.)
Tensile Strength MPa ISO 527-2

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸模量 Tensile Modulus(干燥 dry)
Tensile Modulus MPa ISO 527

拉伸模量 Tensile Modulus(湿润 cond.)
Tensile Modulus MPa ISO 527

断裂伸长率 Elongation at Break
Elongation at Break % ASTM D638

洛氏硬度
Rockwell hardness M 级 ASTM D785

洛氏硬度
Rockwell hardness R 级 ASTM D785

加工方式

注射 Leona™ 1300S Ultramid® A 205F NATURAL 单位测试方法

干燥时间 Hr

干燥温度 °C

水份含量 %

注塑温度模具温度 °C

注塑温度模头温度 °C

注塑温度螺筒中部温度 °C

注塑温度螺筒前部温度 °C

注塑温度螺筒后部温度 °C

注塑成型 Injection Molding Leona™ 1300S Ultramid® A 205F NATURAL 单位测试方法

中段温度 Middle Temperature -Zone 2 ℃

前段温度 Front Temperature -Zone 3 ℃

后段温度 Rear Temperature -Zone 1 ℃

干燥时间 Drying Time hr

干燥温度 Drying Temperature ℃

模具温度 Mold Temperature ℃ ISO 294

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
热性能
电气性能
阻燃性能
冲击性能
机械性能
加工方式
注射
注塑成型 Injection Molding
备注
返回顶部

PA66，Leona™ 1300S对比PA66，Ultramid® A 205F NATURAL对比物性表,价格行情_搜料_soliao